Environment-friendly material for architectural decoration

An environmentally friendly material and architectural decoration technology, applied in the direction of fireproof coatings, coatings, etc., can solve the problems of easy mildew at the construction site of fireproof coatings, endangering the health of personnel, air pollution, etc., to increase practicability, improve moisture absorption, The effect of increasing the adsorption performance

Inactive Publication Date: 2021-01-19
南京市安尔康环境科技有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, due to the high salt content and high humidity in the air in the southeast of my country, the acid rain season in the southwest region, the water vapor is acidic, and the water vapor near the salt lake in the northwest region is salty and alkaline. Mildew occurs, causing air pollution, endangering the health of personnel, and may cause bronchitis, tonsillitis, hay fever, asthma and other respiratory diseases and allergic symptoms caused by mold spores; in order to improve this situation, improve the practicality of coatings and strengthen environmental protection, the present invention proposes an environmentally friendly material for architectural decoration

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027]This embodiment provides an environmentally friendly material for building decoration. The environmentally friendly material is composed of three components of A, B, and C in the ratio of A: B: C = 1.5: 2:5, and A, B, and C include the following components in parts by mass :

[0028]The first component includes the following components in parts by mass: epoxy resin: 23 parts, polyurethane: 4 parts, titanium dioxide: 11 parts, magnesium oxide: 10 parts, diatomaceous earth: 14 parts, glass fiber: 3 parts, Carbon fiber: 14 parts, thixotropic additive: 19 parts, epoxy diacrylate: 4 parts;

[0029]The second component includes the following components by mass parts: modified resin: 16 parts, reinforcing fiber: 3 parts, inorganic filler: 10 parts, active amine: 1 part, PH regulator: 8 parts, silane coupling Agent: 17 parts, auxiliary materials: 22 parts, defoamer: 10 parts, flame retardant: 15 parts;

[0030]The C component includes the following components by mass parts: white cloud: 12 par...

Embodiment 2

[0033]This embodiment provides an environmentally friendly material for building decoration. The environmentally friendly material is composed of three components of A, B, and C in the ratio of A: B: C = 1.5: 2:5, and A, B, and C include the following components in parts by mass :

[0034]The first component includes the following components in terms of parts by mass: epoxy resin: 27 parts, polyurethane: 8 parts, titanium dioxide: 14 parts, magnesium oxide: 13 parts, diatomaceous earth: 19 parts, glass fiber: 6 parts, Carbon fiber: 18 parts, thixotropic additives: 21 parts, epoxy diacrylate: 7 parts;

[0035]The second component includes the following components by mass parts: modified resin: 19 parts, reinforcing fiber: 7 parts, inorganic filler: 14 parts, active amine: 4 parts, PH regulator: 13 parts, silane coupling Agent: 20 parts, auxiliary materials: 27 parts, defoamer: 13 parts, flame retardant: 19 parts;

[0036]The C component includes the following components by mass parts: white c...

Embodiment 3

[0039]This embodiment provides an environmentally friendly material for building decoration. The environmentally friendly material is composed of three components of A, B, and C in the ratio of A: B: C = 1.5: 2:5, and A, B, and C include the following components in parts by mass :

[0040]The first component includes the following components in parts by mass: epoxy resin: 25 parts, polyurethane: 6 parts, titanium dioxide: 12 parts, magnesium oxide: 11 parts, diatomaceous earth: 16 parts, glass fiber: 4 parts, Carbon fiber: 15 parts, thixotropic additive: 20 parts, epoxy diacrylate: 5 parts;

[0041]Component B includes the following components in parts by mass: modified resin: 17 parts, reinforcing fiber: 5 parts, inorganic filler: 12 parts, active amine: 3 parts, PH regulator: 12 parts, silane coupling Agent: 18 parts, auxiliary materials: 25 parts, defoamer: 12 parts, flame retardant: 17 parts;

[0042]The C component includes the following components by mass parts: white cloud: 16 parts, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses an environment-friendly material for architectural decoration. A component A, a component B and a component C are prepared from, by mass, 23-27 parts of epoxy resin, 4-8 partsof polyurethane, 11-14 parts of titanium dioxide, 10-13 parts of magnesium oxide, 14-19 parts of diatomite, 3-6 parts of glass fiber, 14-18 parts of carbon fiber, 19-21 parts of thixotropic additive;4-7 parts of epoxy diacrylate; 16-19 parts of modified resin, 3-7 parts of reinforced fibers, 10-14 parts of an inorganic filling material, 1-4 parts of active amine, 8-13 parts of a pH regulator, 17-20 parts of a silane coupling agent, 22-27 parts of an auxiliary material, 10-13 parts of an antifoaming agent, 15-19 parts of a flame retardant; 12-19 parts of dolomite, 3-6 parts of boron nitride, 20-24 parts of quartz, 12-18 parts of black silicon carbide, 3-7 parts of fine-grain aluminum oxide, 11-16 parts of zinc oxide, 16-19 parts of a delustering agent, 29-33 parts of a solvent, 12-18 partsof a gas-phase corrosion inhibitor, 10-14 parts of a wetting agent and 5-8 parts of a leveling aid.

Description

Technical field[0001]The invention relates to the technical field of environmental protection materials, in particular to an environmental protection material for building decoration.Background technique[0002]At present, due to the high salt content and high humidity in the air in the southeast of China, the acid rain season in the southwest, the acidic water vapor, and the salt lake near the salt lake in the northwestern area, the construction of fireproof coatings in confined spaces is very easy. Mold occurs, causing air pollution, and endangering the health of personnel. It may cause respiratory diseases and allergic symptoms such as bronchitis, tonsillitis, hay fever, asthma, etc. caused by mold spores; in order to improve this situation, improve the practicality of paint Strengthen environmental protection, the present invention proposes an environmental protection material for building decoration.Summary of the invention[0003]The technical problem to be solved by the present i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D4/06C09D4/02C09D7/61C09D7/63C09D7/65C09D5/18
CPCC09D4/06C09D5/18C09D7/61C09D7/63C09D7/65C09D7/70
Inventor 黄海
Owner 南京市安尔康环境科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com