Bin sealing seat slurry matched with PC building component installation and preparation method of bin sealing seat slurry

A building component and supporting technology, which is applied in the field of PC building component installation and matching sealing seat slurry and its preparation, can solve the problems of difficult operation construction, poor waterproof, low strength, etc., and achieve easy operation, fresh slurry, high strength high effect

Pending Publication Date: 2021-02-09
上海卫吉节能科技有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the early stage and at present, some construction projects still use non-specific and non-supporting ordinary mortar for construction, and there are some shortcomings such as cracking, poor waterproofing, low strength, and difficult operation and construction.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] This embodiment provides a kind of PC building component installation matching sealing base slurry, including the following components: Portland cement, quartz sand, redispersible latex powder, active powder and other additives, wherein each component The mass is (the total amount is 1000kg):

[0030] Portland cement: 350kg;

[0031] Quartz sand: 450kg;

[0032] Redispersible latex powder: 80kg;

[0033] Active powder: 60kg;

[0034] Other additives: 20kg.

[0035] As a preferred technical solution of this embodiment, other additives include the following components: low-viscosity cellulose ether water-retaining agent, inorganic fine mineral powder humectant, high-performance polycarboxylate water reducer, high-performance expansion agent, inorganic thixotropic lubricant, Organic starch ether thixotropic agent, wherein the composition ratio of each component is 4.2:4.1:3.7:5.0:4.3:3.4, and other additives can ensure the feasibility of the construction operation and ...

Embodiment 2

[0055] This embodiment provides a kind of PC building component installation matching sealing base slurry, including the following components: Portland cement, quartz sand, redispersible latex powder, active powder and other additives, wherein each component The mass is (the total amount is 1000kg):

[0056] Portland cement: 350kg;

[0057] Quartz sand: 450kg;

[0058] Redispersible latex powder: 80kg;

[0059] Active powder: 60kg;

[0060] Other additives: 20kg.

[0061] As a preferred technical solution of this embodiment, other additives include the following components: low-viscosity cellulose ether water-retaining agent, inorganic fine mineral powder humectant, high-performance polycarboxylate water reducer, high-performance expansion agent, inorganic thixotropic lubricant, Organic starch ether thixotropic agent, in which the composition ratio of each component is 4.8:4.6:4.2:5.5:5.2:4.1, and other additives can ensure the feasibility of the construction operation and t...

Embodiment 3

[0081] This embodiment provides a kind of PC building component installation matching sealing base slurry, including the following components: Portland cement, quartz sand, redispersible latex powder, active powder and other additives, wherein each component The mass is (the total amount is 1000kg):

[0082] Portland cement: 350kg;

[0083] Quartz sand: 450kg;

[0084] Redispersible latex powder: 80kg;

[0085] Active powder: 60kg;

[0086] Other additives: 20kg.

[0087] As a preferred technical solution of this embodiment, other additives include the following components: low-viscosity cellulose ether water-retaining agent, inorganic fine mineral powder humectant, high-performance polycarboxylate water-reducer, high-performance expansion agent, inorganic thixotropic lubricant, Organic starch ether thixotropic agent, wherein the composition ratio of each component is 5.3:5.3:4.6:6.0:6.1:4.8, and other additives can ensure the feasibility of the construction operation and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of bin sealing seat slurry, in particular to bin sealing seat slurry matched with PC building component installation and a preparation method of the bin sealing seat slurry, and the bin sealing seat slurry comprises the following components: Portland cement, quartz sand, redispersible latex powder, active powder and other additives, wherein the proportions of the components are as follows: 35% of Portland cement; 45% of quartz sand; 8% of redispersible latex powder; 6% of active powder; other additives: 2%. The bin sealing seat slurry has excellentthixotropy and good plastic operability, and does not droop, slip or collapse; the early strength is high, and the middle strength and the post strength are continuously and stably increased; after the slurry is cured, the shrinkage rate is low, the texture is compact and hard, and the anti-permeability and anti-deformation capabilities are strong; the product is smooth in construction operability, fresh in slurry and easy to operate, and can be operated for about 1 hour.

Description

technical field [0001] The present invention relates to the technical field of sealing seat slurry, and specifically relates to a sealing seat slurry for PC building component installation and a preparation method thereof. Background technique [0002] PC prefabricated building components are equipped with a matching sealer slurry, which is used to weld the 2-4cm wide gap at the bottom of the component. According to the requirements of the component characteristics, it has high early strength, high strength, extremely low shrinkage and Excellent caulking performance. In the early stage and at present, some of these construction projects still use non-specific and non-supporting ordinary mortar for construction, and there are some shortcomings such as cracking, poor waterproofing, low strength, and difficult operation and construction. In view of this, we propose a kind of PC building component installation matching sealant slurry and its preparation method. Contents of th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B28/04C04B111/27
CPCC04B28/04C04B2111/00293C04B2111/27C04B14/06C04B2103/0057C04B24/383C04B18/141C04B24/38C04B2103/302C04B2103/0068
Inventor 钱卫兵
Owner 上海卫吉节能科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com