Preparation process of high-formability 6111 aluminum alloy automobile plate

A preparation process and technology of aluminum alloy plate, which is applied in the field of metal materials, can solve the problems such as poor stamping and forming effect of 6111 aluminum alloy automobile plate, and achieve the effect of speeding up the lightweight process, good formability, and good uniformity

Inactive Publication Date: 2021-02-19
TIANJIN ZHONGWANG ALUMINUM IND CO LTD
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In view of this, in order to solve the problem that the prior art does not analyze and optimize the r-value and r-value uniformity of the fundamental factors affecting the formability of aluminum alloy automobile sheets, resulting in poor stamping and forming effects of 6111 aluminum alloy automobile sheets, it provides Preparation process of a high formability 6111 aluminum alloy automobile sheet

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation process of high-formability 6111 aluminum alloy automobile plate
  • Preparation process of high-formability 6111 aluminum alloy automobile plate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0026] Such as figure 1 A preparation process for a high formability 6111 aluminum alloy automobile sheet is shown, comprising the following steps:

[0027] A. Ingredients: The aluminum alloy raw materials for the preparation of aluminum alloy plates are mixed according to weight percentage, namely: Si: 0.5-1.0%, Fe: 0.1-0.4%, Cu: 0.6-0.8%, Mn: 0.2-0.4%, Mg : 0.6~0.8%, Cr: 0.10%, Zn: 0.10%, single impurity ≤0.05%, total ≤0.15%, the balance is Al;

[0028] B. Melting and casting: Put the configured aluminum alloy raw materials into the melting furnace in turn for melting. The aluminum alloy raw materials are industrial pure aluminum, industrial pure Mg, industrial pure Zn, master alloy Al-Si, master alloy Al-Cu, master alloy Al -Fe, intermediate alloy Al-Mn, etc., and use flux to refine and cover. After feeding, start stirring when aluminum water appears in the furnace. After stirring evenly, it will be melted into liquid aluminum alloy. The melting temperature is 700-760 ° C....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of metal materials, and relates to a preparation process of a high-formability 6111 aluminum alloy automobile sheet. The process comprises the following steps: casting, three-stage homogenization, hot rolling, annealing, cold rolling, annealing, cold rolling, solid solution quenching and pre-aging. An intermediate annealing process in the cold rolling process is carried out on a continuous annealing line, and the annealing schedule is 480 DEG C / 20 s. Through mutual cooperation of hot rolling, medium annealing and cold rolling processes, An r value excellent in three directions is obtained, the solid solution quenching and pre-aging processes are combined with an existing continuous annealing production line, the process is more suitable for actual industrial production, and finally the high-formability 6111 aluminum alloy automobile plate material capable of being applied to industrial production is obtained.

Description

technical field [0001] The invention belongs to the technical field of metal materials and relates to a preparation process of a highly formable 6111 aluminum alloy automobile plate. Background technique [0002] Under the urgent situation that the world's industrial development requires energy saving and environmental protection, some developed countries have formulated automobile fuel economy regulations and increasingly strict exhaust emission regulations. Therefore, reducing the weight of automobiles to reduce energy consumption, reduce pollution, and improve efficiency has become an important measure for major automobile companies to improve their competitiveness. Aluminum alloy and its processing materials are widely used in the automotive industry due to a series of excellent characteristics such as low density, high specific strength and specific stiffness, good elasticity, good impact resistance, corrosion resistance and good processing performance. important mater...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/02C22C21/08C22C21/18C22F1/043C22F1/047C22F1/057C22C1/03C22C1/06
CPCC22C1/026C22C1/03C22C1/06C22C21/02C22C21/08C22C21/14C22C21/16C22C21/18C22F1/002C22F1/043C22F1/047C22F1/057
Inventor 冉凡青王飞祖立成崔立治张旭鹏白永芳尹竹松
Owner TIANJIN ZHONGWANG ALUMINUM IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com