A kind of thin coating type highly anti-corrosion impregnation coating and its preparation method and application

A dipping coating and corrosive technology, which is applied in the field of thin-coated high-corrosion-resistant dipping coatings and its preparation, can solve the problems of extended construction period, high construction cost, and low construction efficiency, and achieve extended construction time, low cost, and The effect of improving productivity

Active Publication Date: 2022-02-22
SHANGHAI HUAYI FINE CHEM CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

So many paints need to be replaced, such a large paint tank needs to be cleaned, and the workload is heavy. If the construction time limit is short, the frequency of paint replacement and paint tank cleaning will increase, and the construction period will be significantly prolonged due to paint replacement and paint tank cleaning. Low construction efficiency
However, the existing ordinary anti-corrosion coatings are used for impregnation of shield metal embedded parts, and the construction time limit is 7 to 10 days, resulting in high construction costs and low construction efficiency.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of thin coating type highly anti-corrosion impregnation coating and its preparation method and application
  • A kind of thin coating type highly anti-corrosion impregnation coating and its preparation method and application
  • A kind of thin coating type highly anti-corrosion impregnation coating and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] Embodiment 1, the preparation of thin coating type high anti-corrosion impregnation coating A-1

[0055] (1), the preparation of thin coating type high anti-corrosion impregnation paint A-1 comprises the following steps:

[0056] (1), preparation of modified epoxy resin liquid

[0057] Add 30kg cyclohexanone, 25kg methyl isobutyl ketone and 5kg methyl amyl ketone into the reaction kettle, start stirring, control the speed at 100-200 rpm, then slowly add 30kg 901 epoxy resin, and slowly heat up to 80°C, control the stirring speed at 300 rpm, keep warm until the 901 epoxy resin is completely dissolved, cool to 45°C ± 5°C, add 10kg epoxy modified silicone resin SMH-60, control the stirring speed at 300 rpm , until it is stirred into a uniform transparent liquid, the solid content is 36% (m / m), and the material is filtered and discharged with an 80 mesh sieve to obtain a modified epoxy resin liquid.

[0058] (2), preparation of component A

[0059] Add the modified epoxy...

Embodiment 2

[0072] Embodiment 2, the preparation of thin coating type high anti-corrosion impregnation coating A-2

[0073] (1), the preparation of thin coating type high anti-corrosion impregnation coating A-2 comprises the following steps:

[0074] (1), preparation of modified epoxy resin liquid

[0075] Add 20kg of cyclohexanone, 15kg of methyl isobutyl ketone and 7.5kg of methyl amyl ketone into the reaction kettle, start stirring, control the speed at 100-200 rpm, then slowly add 22.5kg of 904 epoxy resin, Slowly heat up to 98°C, stirring at 300 rpm, keep warm until 904 epoxy resin is completely dissolved, cool to 45°C ± 5°C, add 35kg SMH-30 epoxy modified silicone resin, stirring at 300 rpm until it is stirred into a uniform transparent liquid, the solid content is 40% (m / m), and the material is filtered and discharged with an 80 mesh sieve to obtain a modified epoxy resin liquid.

[0076] (2), preparation of component A

[0077] Add 22kg modified epoxy resin solution, 8kg phenol...

Embodiment 3

[0090] Embodiment 3, the preparation of thin coating type high anti-corrosion impregnation coating A-3

[0091] (1), the preparation of thin coating type high anti-corrosion impregnation paint A-3 comprises the following steps:

[0092] (1), preparation of modified epoxy resin liquid

[0093] Add 15kg cyclohexanone, 20kg methyl isobutyl ketone and 5kg methyl amyl ketone in the reactor, start stirring, control the rotating speed to be 100-200 rpm, then slowly add 20kg 909 epoxy resin, slowly Heat up to 140°C, control the stirring speed to 300 rpm, keep warm until the 909 epoxy resin is completely dissolved, cool to 45°C±5°C, add 40kg epoxy modified silicone resin SMH-30, and stir at 300 rpm until it is stirred into a uniform transparent liquid, the solid content is 40% (m / m), and the material is filtered and discharged with an 80 mesh sieve to obtain a modified epoxy resin liquid.

[0094] (2), preparation of component A

[0095] Add 25kg of the modified epoxy resin solution...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a thin coating type impregnating paint with high corrosion resistance, which comprises components A and B, and component A comprises the following components in weight percentage: 15-25% of modified epoxy resin solution; 2-22% of phenolic resin %; Pigment and filler 25-35%; Auxiliary I 2-10%; Solvent I 28-38%; B component contains the following components in weight percentage: Auxiliary II 1-8%; Solvent II 92-99%; The component and the component B are mixed according to the weight ratio of 1:1 to 12:1 and stirred evenly. The preparation method, construction method and application of the above coating are also disclosed. After the coating of the present invention is coated on the surface of metal components, the thickness of the paint film is small, and it has excellent processability, adhesion, mechanical properties, acid resistance and alkali resistance; it also has excellent neutral salt spray resistance and copper resistance. Ion-accelerated salt spray performance; also has a long construction time limit, simple and convenient construction process, energy saving, and low cost.

Description

technical field [0001] The invention belongs to the technical field of coatings, and in particular relates to a thin-coated high-corrosion-resistant dipping coating and a preparation method and application thereof. Background technique [0002] Metal components are made of metal, which have a wide range of applications and various shapes, and play a very important role in engineering. Embedded parts, pipe brackets and suspension brackets are all metal components. The surface of metal components needs to be coated with a layer of paint film to improve its mechanical properties and meet the requirements of its acid resistance, alkali resistance and corrosion resistance. Due to the different shapes of metal components, it is difficult for ordinary spraying and brushing processes to meet the requirements of paint film uniformity and anti-corrosion, so the dip coating process is usually used: the paint is placed in the paint tank, and the entire metal component is dipped in the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D163/00C09D183/04C09D161/06C09D5/08C09D7/61
CPCC09D163/00C09D183/04C09D5/08C09D7/61C08K2003/3045C08K2003/2241C08K2003/328
Inventor 许丽丽苏琴张卫群孙蔚陆静雯
Owner SHANGHAI HUAYI FINE CHEM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com