Multilayer pellet for reducing emission of sintering smoke pollutants

A technology for sintering flue gas and pollutants, applied in the field of multi-layer pellets, can solve the problems of poor emission reduction effect and high cost of flue gas treatment, and achieve the effects of low price, high efficiency of flue gas emission reduction and reasonable technology

Pending Publication Date: 2021-02-26
ANHUI UNIVERSITY OF TECHNOLOGY +1
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The present invention aims at adding ammonia inhibitors in the sintering material in the prior art, which will lead to SO in the sintering process 2 , NO X and dioxin and other pollutants have poor online emission reduction effect and high cost of flue gas treatment; provide a multi-layer pellet for reducing emission of sintering flue g...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Multilayer pellet for reducing emission of sintering smoke pollutants
  • Multilayer pellet for reducing emission of sintering smoke pollutants
  • Multilayer pellet for reducing emission of sintering smoke pollutants

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Such as figure 1As shown, a multi-layer pellet in this embodiment includes an inner layer pellet 100 and a wrapping layer 200; the inner layer pellet 100 includes an inner layer pelletizing material and an ammonia inhibitor, and the ammonia inhibitor Thermal decomposition can release ammonia, and the N element content in the ammonia inhibitor accounts for 0.02-0.15% of the mass of the inner pellet 100, which is 0.047% in this embodiment, and the mass ratio converted into urea is 0.1%; The wrapping layer 200 is wrapped on the outside of the inner layer pellets 100, and the wrapping layer 200 includes the outer pelletizing material; the particle size of the outer layer pelletizing material reaches -0.149mm particle size mass percentage content ≥ 95%; the inner layer pelletizing material The particle size of the material reaches -0.074mm particle size mass percentage content ≥ 95%; the particle size of the inner pellet 100 is 3-5mm; the moisture content of the pellet is 8....

Embodiment 2

[0057] The pellets and sintering emission reduction method of this embodiment are basically the same as those of Embodiment 1, except that the N element content of the ammonia inhibitor in this embodiment accounts for 0.038% of the mass of the inner pellet 100, which is converted into urea The mass ratio is 0.08%, the detection of SO 2 , NO X and the concentration of dioxins are recorded in Table 4, and the desulfurization and denitrification rate and the emission reduction efficiency of dioxins are calculated.

Embodiment 3

[0059] The pellets and sintering emission reduction method of this embodiment are basically the same as those of Embodiment 1, except that the N element content of the ammonia inhibitor in this embodiment accounts for 0.071% of the mass of the inner pellet 100, which is converted into urea The mass ratio is 0.15%, the detection of SO 2 , NO X and the concentration of dioxins are recorded in Table 4, and the desulfurization and denitrification rate and the emission reduction efficiency of dioxins are calculated.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Granularityaaaaaaaaaa
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a multilayer pellet for reducing emission of sintering smoke pollutants, and belongs to the technical field of pollutant emission reduction in the sintering process. The multilayer pellet comprises an inner pellet and a wrapping layer, wherein the inner pellet comprises an inner pelletizing material and an ammonia type inhibitor, the ammonia type inhibitor can release ammonia gas after being heated and decomposed, and the content of the N element in the ammonia type inhibitor accounts for 0.02-0.15% of the mass of the inner pellet. The wrapping layer wraps the outer side of the inner pellet and comprises an outer pelletizing material. The wrapping layer outside the pellet can play a role in preventing NH3 from being released, so that the NH3 can be stably released in a centralized manner at the temperature of 600-800 DEG C, NOX can be discharged at the temperature of 650 DEG C, the discharge temperature of the NOX is consistent with the release temperature interval of NH3, and therefore, the NH3 and the NOX react with each other; and meanwhile, generation of dioxin can be inhibited in the cooling process, the cooling process is conducted until the temperature of the sintering smoke is lowered to be lower than the dioxin synthesis temperature, and the emission reduction efficiency of SO2 and dioxin is improved.

Description

technical field [0001] The invention relates to the technical field of pollutant emission reduction in the sintering process, and more specifically relates to a multilayer pellet used for reducing emission of pollutants in sintering flue gas. Background technique [0002] With the increasingly serious environmental problems and the gradual enhancement of people's awareness of environmental protection, the iron and steel industry, as a major source of pollutant emissions, has received more and more attention from the national environmental protection department. In 2019, my country's Ministry of Ecology and Environment and other five ministries and commissions jointly issued the "Opinions on Promoting the Implementation of Ultra-Low Emissions in the Iron and Steel Industry", requiring iron and steel enterprises across the country to significantly reduce pollutant emission levels, and set the emission standards for sintering / pelletizing process pollutants as particulate matter,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C22B1/24C22B1/16
CPCC22B1/2406C22B1/16
Inventor 龙红明杨涛杨美洲王毅璠钱立新丁龙汪名赫孟庆民余正伟春铁军雷杰王宏涛丁成义
Owner ANHUI UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap