Ultrasonic preparation method of blue-light inorganic bromine-lead-cesium perovskite nanoparticles

A nanoparticle, bromine lead cesium technology, applied in the field of perovskite luminescent nanoparticle preparation, can solve problems such as difficulty in mass synthesis, high temperature heating, etc., and achieve the effects of no high temperature heating, uniform size, and simple synthesis steps

Active Publication Date: 2021-12-14
UNIV OF SCI & TECH OF CHINA
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In view of the above problems, the present invention provides an ultrasonic preparation method of blue-light inorganic bromine-lead-cesium perovskite nanoparticles, which is used to at least partially solve the technical problems of traditional methods that require high temperature heating and are difficult to synthesize in large quantities.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultrasonic preparation method of blue-light inorganic bromine-lead-cesium perovskite nanoparticles
  • Ultrasonic preparation method of blue-light inorganic bromine-lead-cesium perovskite nanoparticles
  • Ultrasonic preparation method of blue-light inorganic bromine-lead-cesium perovskite nanoparticles

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0027] An embodiment of the present invention provides a method for ultrasonically preparing blue-light inorganic bromine-lead-cesium perovskite nanoparticles, including: S1, ultrasonically dissolving cesium acetate and lead acetate in compounds of oleic acid, oleylamine and 1-octadecene , to obtain a precursor solution; S2, adding benzoyl bromide to the precursor solution, and ultrasonically reacting; S3, quenching the reaction in an ice bath, adding ethyl acetate, and centrifuging to obtain bromine-lead-cesium perovskite nanoparticles.

[0028] The method prepares high-efficiency luminescent blue-light inorganic perovskite nanoparticles through ultrasonic synthesis, including: adding cesium acetate and lead acetate to ligands oleic acid and oleylamine, and non-coordinating solvent 1-octadecene; performing ultrasonic to make the solid powder completely Dissolve to form a precursor solution; after adding benzoyl bromide, perform ultrasonication; after ultrasonication, take out ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an ultrasonic preparation method of blue-light inorganic bromine-lead-cesium perovskite nanoparticles, comprising: S1, ultrasonically dissolving cesium acetate and lead acetate in compounds of oleic acid, oleylamine and 1-octadecene to obtain a precursor solution; S2, adding benzoyl bromide to the precursor solution, and ultrasonically reacting; S3, quenching the reaction in an ice bath, adding ethyl acetate, and centrifuging to obtain bromine-lead-cesium perovskite nanoparticles. The present invention prepares highly efficient luminescent blue CsPbBr through a simple ultrasonic synthesis method 3 Nanoparticles have the characteristics of simple method, large-scale preparation, good particle uniformity, and excellent optical properties.

Description

technical field [0001] The invention relates to the technical field of preparation of perovskite luminescent nanoparticles, in particular to an ultrasonic preparation method of blue light inorganic bromine-lead-cesium perovskite nanoparticles. Background technique [0002] Metal halide perovskite semiconductors are promising light-emitting materials for electroluminescent and photoluminescent displays due to their excellent optical properties such as high color purity, easy spectral adjustment, and high luminous efficiency. , and has shown potential as a luminescent probe in bioimaging applications. They exhibit intense and efficient luminescence due to their direct bandgap and tolerance to defects. Perovskites can also be tuned to span the ultraviolet, visible, and near-infrared by controlling the composition of halides that contain iodide, bromide, or chloride. [0003] Although mixed-halide compositions represent a facile approach to bandgap and emission tuning, they of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09K11/66
CPCC09K11/665
Inventor 姚宏斌刘雨莹
Owner UNIV OF SCI & TECH OF CHINA
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com