A high-brightness, colorful technology, applied in the field of preparation of high-brightness colored microspheres, can solve the problems of poor reflective effect of glass beads at night, easy peeling of the color layer of glass beads, poor reflection effect of glass beads, etc., to achieve Excellent reflective effect, good adhesion, and mature production technology

Active Publication Date: 2021-10-22
浙江龙游道明光学有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention aims at the poor reflection effect of glass microspheres in the reflective paint coating in the prior art at night, the poor reflection effect of glass microspheres, the color layer of glass microspheres is easy to fall off, not resistant to solvents, not resistant to scratches, reverse Low reflection performance and other defects provide a new preparation method for high-brightness colored microspheres

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of high-brightness colored microspheres
  • A kind of preparation method of high-brightness colored microspheres

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A preparation method of high-brightness colored microspheres, the preparation method is as follows:

[0043] S1: Take the PET substrate 6 covered with PE film 5 on the surface, pretreat the PET substrate 6 with a guide roller at 150°C, then take the glass beads 1, and implant the glass beads 1 with a bead planting device the surface of the PE film 5, and make the glass microspheres 1 sink into the PE film 5, and the sinking range of the glass microspheres 1 is controlled at 30%;

[0044] S2: Take pigment A, polyester resin, epoxy resin A, isocyanate curing agent A, silane coupling agent, and ethyl acetate and mix them according to the weight ratio of 1:1:1.5:0.2:0.05:3.5 to obtain a mixed Coating A, using a dimple coating device to coat the mixed coating A on the surface of the glass microsphere 1, dry it at a temperature of 110°C, and place it at a temperature of 70°C for aging for 48 hours to form a color layer 2;

[0045] S3: The color layer 2 is placed in an enviro...

Embodiment 2

[0058] A preparation method of high-brightness colored microspheres, the preparation method is as follows:

[0059] S1: Take the PET substrate 6 covered with the PE film 5 on the surface, pretreat the PET substrate 6 with a guide roller at 230°C, then take the glass beads 1, and implant the glass beads 1 with a bead planting device the surface of the PE film 5, and make the glass microspheres 1 sink into the PE film 5, and the sinking range of the glass microspheres 1 is controlled at 50%;

[0060] S2: Take pigment A, polyester resin, epoxy resin A, isocyanate curing agent A, silane coupling agent, and ethyl acetate and mix them according to the weight ratio of 1:1:1.5:0.2:0.05:3.5 to obtain a mixed Coating A, using a dimple coating device to coat the mixed coating A on the surface of the glass microsphere 1, dry it at a temperature of 150°C, and place it at a temperature of 70°C for aging for 48 hours to form a color layer 2;

[0061] S3: Place the color layer 2 in an enviro...

Embodiment 3

[0074] A preparation method of high-brightness colored microspheres, the preparation method is as follows:

[0075] S1: Take the PET substrate 6 covered with PE film 5 on the surface, pretreat the PET substrate 6 with a guide roller at 190°C, then take the glass beads 1, and implant the glass beads 1 with a bead planting device the surface of the PE film 5, and make the glass microspheres 1 sink into the PE film 5, and the sinking range of the glass microspheres 1 is controlled at 40%;

[0076] S2: Take pigment A, polyester resin, epoxy resin A, isocyanate curing agent A, silane coupling agent, and ethyl acetate and mix them according to the weight ratio of 1:1:1.5:0.2:0.05:3.5 to obtain a mixed Coating A, using a dimple coating device to coat the mixed coating A on the surface of the glass microsphere 1, dry it at a temperature of 130°C, and place it at a temperature of 70°C for aging for 48 hours to form a color layer 2;

[0077] S3: The color layer 2 is placed in an enviro...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing high-brightness colored microspheres. The preparation method is as follows: S1: implant glass microspheres on the surface of PE film; S2: prepare a mixed coating A, and apply the mixed coating A on the surface of the glass microspheres , forming a color layer; S3: coating the metal layer on the surface of the color layer; S4: preparing the mixed coating B, coating the mixed coating B on the surface of the metal layer to obtain a composite reflective film; S5: taking the composite reflective film, and The glass microspheres are peeled off from the PET substrate and PE film, and then crushed and separated by rolling rollers to obtain colored particles; S6: Metal iron microspheres are mixed with colored particles, followed by high-speed ball milling to obtain Colored microspheres; S7: Sieve the colored microspheres to obtain high-brightness colored microspheres. The colored microspheres prepared by the invention not only have the effect of colored reflection, but also have the best retroreflective performance, and finally the glass microspheres in the reflective paint coating can achieve an excellent colored light effect at night, which overcomes the defects in the prior art.

Description

technical field [0001] The invention relates to reflective materials, in particular to a preparation method of high-brightness colored microspheres. Background technique [0002] The existing reflective paint is generally made of acrylic resin as the base material, mixed with a certain proportion of directional reflective material in a solvent, which belongs to a new type of reflective paint. The principle of reflective paint is to pass the irradiated light through reflective glass beads Reflected back into the human line of sight, forming a reflective effect. However, the reflective effect of reflective paint at night is very poor. Since the glass beads used are high-emissivity glass beads, the resin, pigment, and glass beads are mixed and sprayed and brushed to make a reflective paint coating. The focal position of the beads cannot be adjusted for optimal reflection, so the reflective paint coating is very poor at night. [0003] Part of the colored glass beads currently...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09D5/33C09D163/00C09D167/00C09D7/63C09D133/04
CPCC09D5/004C09D163/00C09D7/63C08L67/00C08L33/04C08K5/54
Inventor 吴伟斌刘玫胡锋舒林飞苏国芳
Owner 浙江龙游道明光学有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka