Synthetic blended fabric and clothes

A technology of synthetic fiber and cloth, which is applied in the field of suits and suits, can solve the problems of easy wrinkles and high prices, and achieve the effect of reducing manufacturing costs

Inactive Publication Date: 2021-04-09
ITOI LIFESTYLE RES
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] On the other hand, there is a problem that 100 mass% wool suit clothing is prone to wrinkle when it is left in a wet state and dried, and when it is washed in a household washing machine and spin-dried.
In addition, wool as a raw material is more expensive than synthetic fibers, so suits made of 100% wool by mass are expensive

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Synthetic blended fabric and clothes

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0058] As wool, one having a fiber diameter of 18.5 μm was prepared. As the polyester fiber, a polyethylene terephthalate wool bundle having a fineness of 2.2 dtex was prepared. As the ultrafine AC fiber, a polyacrylonitrile fiber tow having a fineness of 1.1 dtex was prepared. Using these fibers as raw materials, in the aforementioned spinning process, blending was carried out at a mixing ratio in which the wool content was 35% by mass, the polyester fiber content was 40% by mass, and the ultrafine AC fiber content was 25% by mass, to obtain a metric count of 1 / 80, blended yarn (single yarn) with twist number Z of 1000T / m. Two of these single yarns were combined, and further twisted by Z twisting 1100 times per 1 m (final twist number Z was 1100 T / m) to obtain a blended yarn (two-ply yarn). Using this blended yarn (two-ply yarn), according to figure 1 The weave shown in the weave was carried out, and the textile finishing process was carried out by a conventional method t...

Embodiment 2

[0060] By the same raw material and mixing ratio as in Example 1 (the content of each fiber in the blended yarn is the same), the blended yarn (single yarn) with a metric count of 1 / 80 (primary twist number S is 1000T / m) was obtained. . Two of these blended yarns (single yarns) were joined together and twisted 1100 times per 1 m in S twist (the number of final twist S was 1100 T / m). The cloth described in Example 2 was obtained by weaving a cloth in the same manner as in Example 1 using the obtained blended yarn (two-ply yarn).

[0061] The fabrics obtained in Example 1 and Example 2 were all good in resilience, and had a good feel equivalent to that of 100% by mass wool suiting. In addition, these fabrics have a unique smooth feel on the surface, non-sticky and dry comfortable touch like the unique touch of 100% wool suiting, and have the unique color gradation of 100% wool suiting The same level of color. Therefore, the fabrics obtained in Example 1 and Example 2 are suit...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Basis weightaaaaaaaaaa
cover factoraaaaaaaaaa
Login to View More

Abstract

Provided is a synthetic blended fabric which is made of a blended yarn in which at least three kinds of fiber including wool, a polyester fiber, and an acrylic fiber are blended, or which is mainly comprised of the blended yarn, wherein at least three kinds of fibers are mixed and almost uniformly distributed at a predetermined mixing ratio along the longitudinal direction of the blended yarn, the total content of the wool, the polyester fiber, and the acrylic fiber in the blended yarn is 90-100 mass%, and the fineness of the acrylic fiber is 0.5-1.4 dtex. The synthetic blended fabric has a high-class feeling equivalent to products made of 100 mass% of wool, is less likely to wrinkle upon drying, even after becoming wet from water or being washed in a household washing machine, and is less likely to lose firmness or tension upon treatment with steam.

Description

technical field [0001] The present invention relates to a synthetic fiber-containing cloth (hereinafter also referred to as "synthetic fiber-containing cloth") and a suit using the synthetic fiber-containing cloth as a suit lining. Background technique [0002] Wool (wool) 100% by mass suit material has a good hand feeling, the apparent color is layered, and the sense of quality is good. The appearance of the material is smooth but has a sense of three-dimensionality and layering. Therefore, suiting materials for men or women's suits made of 100% by mass of wool are recognized as high-end products with high commodity value. Suiting materials made of strong-twisted yarn using fine wool have a more luxurious feel and are recognized as having higher commodity value. [0003] Generally speaking, good hand feeling as a material for men's suits and the like refers to good drapability, good resilience and unique touch. Drapability is the property of the suit material to wrap it s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D03D15/47D03D15/233D03D15/283A41D31/00D02G3/04
CPCD02G3/04D10B2331/04D10B2211/01D10B2321/10D10B2211/02D03D15/233D03D15/283D03D15/47D03D15/41D03D13/004D10B2201/02D10B2321/08
Inventor 糸井徹
Owner ITOI LIFESTYLE RES