Light anti-bending and anti-torsion bionic composite material and preparation method thereof

A biomimetic composite material, bending and twisting technology, applied in chemical instruments and methods, synthetic resin layered products, transportation and packaging, etc., can solve the problems of large weight, low bending and torsional strength, poor chemical stability, etc., and achieve small specific gravity , Larger specific strength and larger specific modulus

Active Publication Date: 2021-04-30
JILIN UNIV
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In view of the deficiencies in the prior art above, the purpose of the present invention is to provide a light-weight bending-torsion-resistant bionic composite material and its preparation method, aiming at solving the problems of insufficient specific stiffness, heavy weight, and low bending-torsion strength of traditional metal materials, and Poor chemical stability, easy to corrode, difficult to meet the needs of industry development

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Light anti-bending and anti-torsion bionic composite material and preparation method thereof
  • Light anti-bending and anti-torsion bionic composite material and preparation method thereof
  • Light anti-bending and anti-torsion bionic composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0034] The present invention provides a light-weight bending-resistant bionic composite material and its preparation method. In order to make the purpose, technical solution and effect of the present invention clearer and clearer, the present invention will be further described in detail below. It should be understood that the specific embodiments described here are only used to explain the present invention, not to limit the present invention.

[0035]There are many light-weight, high-strength, high-toughness, high specific stiffness, and bending-torsion-resistant materials in nature for researchers to study and study, get inspiration from them, and carry out combined bionic design for daily design and manufacturing. As a flying animal, bird far exceeds other flying animals such as mammals (bats) and insects in terms of efficiency and time. Studies have shown that the reason why birds have such efficient flight capabilities is due to the structural properties of their feather...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a light anti-bending and anti-torsion bionic composite material and a preparation method thereof. The composite material comprises a bottom layer, a lower partition plate layer, a hollow structure middle layer, an upper partition plate layer and an outer layer which are sequentially arranged in a stacked mode from bottom to top; the hollow structure middle layer comprises a first-stage dense hole structure, a loose hole upper-layer structure, a first-stage loose hole structure, a loose hole lower-layer structure and a second-stage dense hole structure which are sequentially stacked from bottom to top; and the first-level compact pore structure, the first-level loose pore structure and the second-level compact pore structure are each composed of a woven fiber resin layer, and each woven fiber resin layer is formed by alternately winding weft-wise fibers and warp-wise fibers on a core film. The middle layer of the hollow structure is arranged in the mode that the outside is dense and the inside is sparse, the weight of the material can be reduced, the specific rigidity of the material can be improved, when the material is bent, the upper surface of the middle layer of the hollow structure bears tensile stress, the lower surface of the middle layer of the hollow structure bears tensile pressure, and the bending resistance and toughness of the material are improved.

Description

technical field [0001] The invention relates to the technical field of new materials, in particular to a light-weight bending-torsion-resistant bionic composite material and a preparation method thereof. Background technique [0002] With the development of modern science, aviation, aerospace, rail transit, biomedicine and other fields have put forward higher requirements for engineering materials. Composite materials have excellent characteristics of small specific gravity, high specific strength and high specific modulus. In some On the one hand, it has more excellent characteristics than metal materials. Moreover, many characteristics of biological materials in nature are worth learning. For example, birds need to face complex turbulence when flying in the air for a long time, so they have evolved unique lightweight and high-strength structures to meet complex environmental conditions. Bird feathers are an extremely lightweight material that spans multiple scales, from n...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B9/00B32B9/04B32B17/02B32B17/12B32B27/02B32B27/12B32B3/08B32B37/00B32B37/06B32B37/10
CPCB32B5/02B32B5/26B32B3/08B32B37/00B32B37/06B32B37/10B29C70/24B29C70/34B29C70/54B29C70/543B32B2262/106B32B2262/101B32B2262/10B32B2262/0269B32B2307/544B32B2307/546B32B2307/558B32B2605/08B32B2605/18B32B2605/10
Inventor 韩志武张芷嫣穆正知张斌杰王宇飞宋文达李玉姣张爽李健豪李博张俊秋牛士超
Owner JILIN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products