Powder coating with metal effect and preparation method thereof

A powder coating and metal effect technology, applied in powder coatings, polyester coatings, coatings, etc., can solve the problems of broken aluminum powder, weather resistance and chemical resistance, etc., to achieve good surface smoothness and excellent Performance, Guaranteed Consistency Effect

Active Publication Date: 2021-04-30
艾勒可新材料(佛山)有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Using the patented method, the aluminum powder will be broken and the aluminum powder will be exposed directly, so the weather resistance and chemical resistance will be greatly reduced

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Powder coating with metal effect and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0030] The invention provides a method for preparing a powder coating with a metallic effect, comprising:

[0031] (1) Pre-mix the raw materials evenly, and extrude and pulverize to obtain the base powder, the average particle size of the base powder is controlled at 20-55 μm;

[0032] The raw materials of the primer include: 40-90wt% resin, 5-50wt% curing agent, 0.1-10wt% auxiliary agent, 0-20wt% pigment, 0-20wt% filler. Preferably, the raw materials of the primer include: 50-70wt% resin, 5-30wt% curing agent, 0.1-10wt% auxiliary agent, 0-20wt% pigment and 0-15wt% filler.

[0033] Wherein, the melt viscosity of the resin at 160° C. is 1500-8000 cps, which can ensure that the film-forming substance in the paint can fully infiltrate with the metal powder, and ensure leveling and surface smoothness. If the melt viscosity of the resin is outside the above range, when the powder coating melts, the viscosity is too high or it is not easy to melt, and when the powder coating passes...

Embodiment 1

[0069] (1) Mix the raw materials in advance, and crush them through extrusion to obtain a base powder with a particle size of 20-45 μm; wherein, the raw materials of the base powder include: 65wt% resin, 5wt% curing agent, 1.3wt% auxiliary agent, 15.2 wt% pigment and 13.5wt% filler; the resin is selected from Allnex Corporation Crycoat 2441-2, the curing agent is selected from Japan Nissan TEPIC-G curing agent, and the auxiliary agent is selected from 1wt% leveling agent (Estron Corporation Resiflow PV88) and 0.3wt% Benzoin, pigment selects 15wt% titanium dioxide and 0.2wt% carbon black for use, and filler selects barium sulfate for use;

[0070] (2) adding metal powder in proportion, and mixing the metal powder and the base powder evenly, wherein the metal powder is added in an amount of 6 wt%, and its average particle size is 40-50 μm;

[0071] (3) Melting the mixed powder coating containing metal powder through a two-roll kneader, the temperature of the two-roll kneader is ...

Embodiment 2

[0074] (1) Mix the raw materials evenly in advance, and crush them by extrusion to obtain a base powder of 20-55 μm; wherein, the raw materials of the base powder include: 65wt% resin, 5wt% curing agent, 1.3wt% auxiliary agent, 15.2wt% pigment And 13.5wt% filler; Described resin selects Crycoat 2441-2 of Allnex Company for use, curing agent selects Japanese Nissan TEPIC-G curing agent for use, auxiliary agent selects 1wt% leveling agent (Estron Company Resiflow PV88) and 0.3wt% benzoin for use, pigment Select 15wt% titanium dioxide and 0.2wt% carbon black, and use barium sulfate as filler;

[0075] (2) adding metal powder in proportion, and mixing the metal powder and the base powder evenly, wherein the metal powder is added in an amount of 10wt%, and its average particle size is 35-60 μm;

[0076] (3) Melting the mixed powder coating containing metal powder through a two-roll kneader, the temperature of the two-roll kneader is set to 150°C, and the gap between the two rolls i...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a powder coating with a metal effect, wherein the preparation method comprises the steps: (1) premixing raw materials uniformly, and extruding and crushing to obtain base powder; (2) adding metal powder according to the proportion, and mixing the metal powder and base powder evenly, wherein the adding amount of the metal powder is 4-30 wt%; (3) carrying out melting treatment on the mixed powder coating containing the metal powder through a mixing mill, wherein the temperature of the mixing mill is set to be 130 DEG C to 170 DEG C, and the melting treatment temperature is higher than the melting point or softening point of the base powder and lower than the curing temperature of the base powder; and (4) cooling and crushing the molten powder coating again to obtain the powder coating with the metal effect. Correspondingly, the invention further provides the powder coating with the metal effect, wherein the powder coating is prepared by the method. By the adoption of the method, the content of the added metal powder is large, the flicker degree of metal can be guaranteed, it can also be guaranteed that the consistency of spraying colors is good, and stability is high.

Description

technical field [0001] The invention relates to the technical field of powder coatings, in particular to a powder coating with metallic effects and a preparation method thereof. Background technique [0002] Powder coating is a new type of solvent-free 100% solid coating, does not contain VOC, and is an environmentally friendly coating. Powder coatings are prepared by mixing resins, pigments, fillers, curing agents and other additives in a certain proportion, and then through hot extrusion, crushing and sieving. They are stable in storage at room temperature. After electrostatic spraying, friction spraying or fluidized bed dipping, they are heated and baked to melt and solidify to form a flat and bright permanent coating film to achieve the purpose of decoration or anti-corrosion. Powder coatings have developed very rapidly in the past 40 years. At present, the annual sales volume of powder coatings in the Chinese market is about 1 million tons, and the annual growth rate i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/00C09D5/03C09D7/61
CPCC09D167/00C09D5/033C09D5/032C09D5/035C08K2003/2241C08K2003/3045C08K3/22C08K3/04C08K3/30C08K3/08
Inventor 伍明
Owner 艾勒可新材料(佛山)有限公司