Waterproof geopolymer material and preparation method thereof

A geopolymer and waterproof technology, applied in the field of waterproof geopolymer materials and their preparation, can solve the problems of high price, difficult to popularize and use, poor durability, etc., and achieve low cost, good shrinkage resistance, and improved resistance to osmotic effect

Active Publication Date: 2022-04-15
WUHAN UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the price of above-mentioned many crack repairing materials is relatively expensive, and durability is very poor, is difficult to popularize and use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterproof geopolymer material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] In this embodiment, the preparation process of the waterproof polymer material is as follows:

[0032] Put 0.06 parts of modified nano-magnesium oxide and 0.08 parts of dispersant in 9 parts of water, stir for 240s, and then put it under the power of 700W for 0.5h to obtain a uniform mixed solution; then weigh 40 parts of fly ash, 26 Pour phosphorus slag, 10 parts of ordinary Portland cement, 7 parts of sodium bentonite into the mixing pot, stir for 90 seconds to obtain the mixture particles, then mix the obtained mixture particles, 0.01 parts of admixture, 4 parts of sodium hydroxide solid and Add 5 parts of sodium silicate solids into the muffle furnace (setting temperature is 800°C), calcinate for 5 hours, sieve after cooling to obtain geopolymer colloid powder; then add the homogeneous mixed solution obtained above to the above geopolymer Stir in the colloidal powder for 240s to obtain a geopolymer slurry, then pour, vibrate, and cure under natural conditions to obt...

Embodiment 2

[0036] In this embodiment, the preparation process of the waterproof polymer material is as follows:

[0037] Put 0.07 parts of modified nano-magnesium oxide and 0.08 parts of dispersant in 10 parts of water, stir for 240s, and then put it under the power of 700W for 0.5h to obtain a uniform mixed solution; then weigh 39 parts of fly ash, 26 Pour 10 parts of phosphorus slag, 10 parts of ordinary Portland cement, and 6 parts of sodium bentonite into the mixing pot, stir for 90 seconds to obtain the mixture particles, and then mix the obtained mixture particles, 0.01 parts of admixture, 5 parts of sodium hydroxide solid and Add 5 parts of sodium silicate solid into the muffle furnace (setting temperature is 900°C), calcinate for 6 hours, sieve after cooling to obtain geopolymer colloidal powder; then add the homogeneous mixed solution obtained above to the above geopolymer Stir in the colloidal powder for 120s to obtain a geopolymer slurry, then pour, vibrate, and maintain under...

Embodiment 3

[0039] In this embodiment, the preparation process of the waterproof polymer material is as follows:

[0040]Put 0.06 parts of modified nano-magnesium oxide and 0.08 parts of dispersant in 9 parts of water, stir for 240s, and then put it under the power of 700W for 0.5h to obtain a uniform mixed solution; then weigh 40 parts of fly ash, 26 Pour phosphorus slag, 10 parts of ordinary Portland cement, 7 parts of sodium bentonite into the mixing pot, stir for 90 seconds to obtain the mixture particles, then mix the obtained mixture particles, 0.01 parts of admixture, 4 parts of sodium hydroxide solid and Add 5 parts of sodium silicate solids into the muffle furnace (setting temperature is 800°C), calcinate for 5 hours, sieve after cooling to obtain geopolymer colloid powder; then add the homogeneous mixed solution obtained above to the above geopolymer Stir in the colloidal powder for 240s to obtain a geopolymer slurry, then pour, vibrate, and cure under natural conditions to obta...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a waterproof polymer material and a preparation method thereof. The invention is composed of raw materials such as fly ash and ordinary portland cement, and is composed of admixtures such as nano-magnesium oxide, and the geopolymer has good construction performance, and at the same time has compressive strength, good bonding strength development, and shrinkage performance. Good, good impermeability and other characteristics. The invention can make full use of fly ash solid waste, not only can solve the problem of solid waste stacking, and turn waste into treasure, but also the prepared waterproof geopolymer material can be used for repairing cracks in tunnel lining and other parts. The waterproof geopolymer material of the present invention omits the configuration process of the alkali excitation solution, realizes normal temperature preparation, and has a simple preparation method, low cost, and is easy to popularize.

Description

technical field [0001] The invention relates to the technical field of geopolymer-based materials, in particular to a waterproof geopolymer material and a preparation method thereof. Background technique [0002] "Ten Tunnels and Nine Cracks" describes the general situation of cracks in tunnels today. Tunnel cracks are the main cause of tunnel water leakage and other diseases, and are also common diseases in tunnel construction and operation. Among the many diseases and problems in tunnels, cracks in tunnel lining structure are relatively common, and they are more harmful. The occurrence and development of cracks not only promote each other with water leakage and regional deterioration of lining, but also directly affect the quality of tunnels. The safe bearing of the lining structure forms a vicious circle and accelerates the destruction process of the lining structure. At present, the treatment measures for tunnel lining cracks include two aspects. One is to improve the s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/04C04B111/27C04B111/72
CPCC04B28/04C04B2201/50C04B2111/72C04B2201/10C04B2111/27C04B2111/00724C04B2111/00017C04B18/08C04B18/145C04B14/104C04B22/062C04B22/00C04B22/066C04B24/26C04B24/2652C04B24/04C04B24/124C04B2103/408
Inventor 李杉李发平卢亦焱陈淼杨哲铭程志军陈得锋
Owner WUHAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap