Preparation method of novel high-leveling-property cast iron alcohol-based casting coating
A casting coating and leveling technology, applied to casting molding equipment, coatings, cores, etc., can solve problems such as poor surface quality of castings, excessive flow marks, and difficult flow coating operations for workers
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0023] A preparation method of a novel high-leveling cast iron alcohol-based casting coating, characterized in that it comprises the following steps:
[0024] ① Put the carrier methanol and xylene into the high-speed disperser, start stirring, and the stirring speed is 1000 rpm;
[0025] ②The pretreatment and preparation steps of the composite suspending agent are as follows:
[0026] The mixing of a suspending agent: the lithium-based bentonite that is 10 parts by weight, the magnesium aluminum silicate that is 8 parts by weight, the attapulgite that is 8 parts by weight and the demineralized water that is 25 parts by weight Use a kneader to shear and stir for 30-50 minutes, and then let it stand for more than 48 hours to prepare a mixed suspension paste;
[0027] The emulsification of b suspending agent: the mixed suspending agent paste in step a is mixed with the alcohol that parts by weight are 150 parts, add SF-720 leveling agent, emulsify 1 hour with emulsifying machine...
Embodiment 1
[0041] A preparation method of a novel high-leveling cast iron alcohol-based casting coating, characterized in that it comprises the following steps:
[0042] ① Put the carrier methanol and xylene into the high-speed disperser, start stirring, and the stirring speed is 1000 rpm;
[0043] ②The pretreatment and preparation steps of the composite suspending agent are as follows:
[0044] The mixing of a suspending agent: the lithium-based bentonite that is 10 parts by weight, the magnesium aluminum silicate that is 8 parts by weight, the attapulgite that is 8 parts by weight and the demineralized water that is 25 parts by weight Use a kneader to shear and stir for 30 minutes, and then let it stand for more than 48 hours to prepare a mixed suspension paste;
[0045] The emulsification of b suspending agent: the mixed suspending agent paste in step a is mixed with the alcohol that parts by weight are 150 parts, add SF-720 leveling agent, emulsify 1 hour with emulsifying machine, m...
Embodiment 2
[0059] A preparation method of a novel high-leveling cast iron alcohol-based casting coating, characterized in that it comprises the following steps:
[0060] ① Put the carrier methanol and xylene into the high-speed disperser, start stirring, and the stirring speed is 1000 rpm;
[0061] ②The pretreatment and preparation steps of the composite suspending agent are as follows:
[0062] The mixing of a suspending agent: the lithium-based bentonite that is 10 parts by weight, the magnesium aluminum silicate that is 8 parts by weight, the attapulgite that is 8 parts by weight and the demineralized water that is 25 parts by weight Use a kneader to shear and stir for 30 minutes, and then let it stand for more than 48 hours to prepare a mixed suspension paste;
[0063] The emulsification of b suspending agent: the mixed suspending agent paste in step a is mixed with the alcohol that parts by weight are 150 parts, adds SF-720 leveling agent, emulsifies with emulsifying machine 1 hour...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap