In-situ synthesis aluminum matrix composite system with permanent magnet stirring function

An aluminum-based composite material and permanent magnet stirring technology, which can be used in stirring devices, furnaces, charge control and other directions, and can solve problems such as high temperature oxidation resistance

Pending Publication Date: 2021-05-18
ALUMICS MATERIALS INST SHANGHAI JIAO TONG UNIV (ANHUI HUAIBEI) +1
View PDF8 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] At present, most of the aluminum melt degassing rotors are made of graphite material, because graphite material has excellent thermal shock resistance and can be machined, and aluminum liquid does not infiltrate graphite, but the weakness of graphite material is that it is not resistant to high temperature oxidation, resulting in long service life. Only need to replace in 14-20 days

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • In-situ synthesis aluminum matrix composite system with permanent magnet stirring function
  • In-situ synthesis aluminum matrix composite system with permanent magnet stirring function
  • In-situ synthesis aluminum matrix composite system with permanent magnet stirring function

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Such as figure 1 As shown, the pure aluminum or aluminum alloy substrate is melted at 700-760° C., the aluminum melting furnace 1 containing the aluminum melt 2 is placed on the hydraulic lifting table 10, and reaction salts and reaction aids are added for reaction. The hydraulic lifting table 10 is raised so that the dip tube 5 of the vacuum bag 3 arranged above the aluminum melting furnace 1 is immersed into the aluminum melt 2 . The vacuum chamber 8 of the vacuum bag 3 is evacuated through the pumping port 4, so that the aluminum melt 2 enters the vacuum bag 3 under atmospheric pressure.

[0041]At the same time, the aluminum melt is sprayed with argon rotation: the graphite rotor is lowered, and the rotating rod 6 of the graphite rotor passes through the sealed bearing 7 arranged on the top of the vacuum bag 3, passes through the vacuum chamber 8, and inserts the nozzle 9 into the bottom of the aluminum melt 2. At the bottom, argon gas is blown in through the middl...

Embodiment 2

[0050] Such as figure 2 As shown, the pure aluminum or aluminum alloy substrate is melted at 700-760°C, the aluminum melt 2 is placed in the aluminum melting furnace 1, and reaction salts and reaction aids are added for reaction. The immersion tube 5 of the vacuum bag 3 arranged above the aluminum melting furnace 1 is immersed into the aluminum melt 2 . The vacuum chamber 8 of the vacuum bag 3 is evacuated through the pumping port 4, so that the aluminum melt 2 enters the vacuum bag 3 under atmospheric pressure.

[0051] At the same time, the aluminum melt is sprayed with argon rotation: the graphite rotor is lowered, and the rotating rod 6 of the graphite rotor passes through the sealed bearing 7 arranged on the top of the vacuum bag 3, passes through the vacuum chamber 8, and inserts the nozzle 9 into the bottom of the aluminum melt 2. At the bottom, argon gas is blown in through the middle hole of the rotating rod 6 and ejected from the rotating nozzle 9. The formed bubbl...

Embodiment 3

[0061] Such as image 3 As shown, the pure aluminum or aluminum alloy substrate is melted at 700-760°C, the aluminum melt 2 is placed in the aluminum melting furnace 1, and reaction salts and reaction aids are added for reaction. The immersion tube 5 of the vacuum bag 3 arranged above the aluminum melting furnace 1 is immersed into the aluminum melt 2 . The vacuum chamber 8 of the vacuum bag 3 is evacuated through the pumping port 4, so that the aluminum melt 2 enters the vacuum bag 3 under atmospheric pressure.

[0062] At the same time, the aluminum melt is sprayed with argon rotation: the graphite rotor is lowered, and the rotating rod 6 of the graphite rotor passes through the sealed bearing 7 arranged on the top of the vacuum bag 3, passes through the vacuum chamber 8, and inserts the nozzle 9 into the bottom of the aluminum melt 2. At the bottom, argon gas is blown in through the middle hole of the rotating rod 6 and ejected from the rotating nozzle 9. The formed bubble...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses an in-situ synthesis aluminum-based composite material system with a permanent magnet stirring function. The system comprises an aluminum smelting furnace containing aluminum melt, a vacuum bag, a graphite rotor and a permanent magnet stirring device; the vacuum bag is provided with an immersion pipe and an extraction opening, and the immersion pipe is arranged to be capable of being immersed into the aluminum melt in the aluminum smelting furnace; and the graphite rotor is used for argon rotary injection, the graphite rotor is provided with a rotating rod and a spray head, the rotating rod is arranged to penetrate through a vacuum chamber of the vacuum bag through a sealing bearing arranged at the top of the vacuum bag, the spray head is inserted into the bottom of the aluminum melt, the rotating rod comprises an inner pipe and an outer pipe, the outer pipe is connected with an argon blowing pipe through a rotating joint, the inner pipe is connected with a powder conveying bin, and the powder conveying bin is connected with a powder conveying gas pipe; and the permanent magnet stirring device is arranged below the aluminum smelting furnace.

Description

technical field [0001] The invention relates to aluminum-based composite materials, in particular to the preparation of in-situ self-generated aluminum-based composite materials. Background technique [0002] The in-situ self-generated aluminum matrix composite material is to use the chemical reaction between different elements or chemicals under certain conditions to generate one or several ceramic phase particles in the aluminum matrix to achieve the purpose of improving the performance of a single metal alloy. The composite material prepared by in-situ self-generation has no pollution on the surface of the reinforcement, and the compatibility between the matrix and the reinforcement is good. By selecting the reaction type and controlling the reaction parameters, different types and quantities of in-situ reinforced particles can be obtained. [0003] However, the in-situ self-generated aluminum matrix composites have high requirements on the conditions including degassing...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B22D41/58C21C7/072B22D1/00C21C7/10F27D27/00
CPCB22D41/58C21C7/10C21C7/072B22D1/002F27D27/00F27D2027/002C22B9/05C22B21/068C22B9/04C22B9/10B22D1/005F27D2003/169F27D2003/168F27D3/16
Inventor 王浩伟王建中李爱平
Owner ALUMICS MATERIALS INST SHANGHAI JIAO TONG UNIV (ANHUI HUAIBEI)
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap