Lenzing modal-combed cotton blended plain weave fabric and production method thereof

A technology of refined modal fine and plain weave fabrics, which is applied in textiles, fabrics, textiles and papermaking, etc., can solve the problems of lack of high-efficiency and high-quality Lenzing modal combed cotton blended yarn fiber production methods, and achieve the effect of not being brittle

Inactive Publication Date: 2021-06-01
JIHUA 3509 TEXTILE
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The object of the present invention is to provide a kind of Lenzing Modal combed cotton blended plain weave fabric and its production method, which is used to solve the problem of lack of high-efficiency and high-quality Lenzing Modal combed cotton blended yarn fiber production method in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The parameters of the Lenzing Modal combed cotton blended plain weave fabric prepared in this embodiment are: the specification of the warp yarn is 52% MODAL and 48% JC, the tex number is 6.5tex, spun by compact spinning, The yarn strength is 120N; the weft yarn specifications are: 52% MODAL and 48% JC, the tex number is 6.5tex, and the yarn strength is 120N; the warp density of Lenzing Modal combed cotton blended plain weave fabric is 716 threads / 10cm , the weft density is 512 threads / 10cm, and the width is 269cm.

[0026] The preparation steps of the above-mentioned Lenzing Modal combed cotton blended plain weave fabric are specifically:

[0027] (1) Warping process: adopt the front, middle and rear segmental method to configure the tension. The tension disc at the side is 4g more than the tension disc at the front section. Align the two sides 5m before driving and there is no thinning or folding. The speed is preferably 440m / min.

[0028] (2) Sizing process: Take ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Yarn strengthaaaaaaaaaa
Strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses Lenzing modal-combed cotton blended plain weave fabric and a production method thereof. The Lenzing modal-combed cotton blended plain weave fabric is formed by interweaving warp yarn and weft yarn, wherein the specification of the warp yarn is 52% of MODAL and 48% of JC, the special number is 6.5 tex, the warp yarn is spun in a compact spinning mode, and the yarn strength is not less than 110 N. The specification of the weft yarn is as follows: 52% of MODAL and 48% of JC, the special number is 6.5 tex, and the strength of the yarns is not less than 110 N; the warp density of the Lenzing modal-combed cotton blended plain weave fabric is 716-716.5 pieces per 10 cm, the weft density of the same is 511-512 pieces per 10 cm, and the breadth of the same is 269-269.5 cm. By adopting the proper proportion of Lenzing modal to combed cotton, adjusting the yarn strength and selecting proper mortar and weaving parameters, the efficient and high-quality Lenzing modal-combed cotton blended plain weave fabric can be produced, the fabric is not prone to brittle fracture, the first-grade product rate put in storage is 99.5% or above, and the weaving efficiency reaches 92% or above.

Description

technical field [0001] The invention relates to the technical field of textiles, in particular to a Lenzing Modal combed cotton blended plain weave fabric and a production method thereof. Background technique [0002] Lenzing Modal is a textile fabric developed by the Austrian Lenzing Company in the 1980s. It is a new type of regenerated cellulose fiber developed earlier. Due to the high price of the fiber at the beginning of development, the performance has not been fully understood and other reasons, it has not been mass-produced. Until the end of the last century, with the improvement of people's living standards, the requirements for wearing comfort gradually increased, and intimate clothing made of modal fibers entered the family. [0003] Lenzing Modal combed cotton blended yarn fiber is a high wet modulus fiber. The fiber raw material comes from wood. Its manufacturing process is non-polluting and the product is biodegradable. It is the most typical green fiber. How...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D03D15/217D03D15/225D03D13/00D06M15/11D06M101/06
CPCD03D15/00D03D13/008D06M15/11D06M2101/06
Inventor 余拓刘渊明余胜熊原王亚锋
Owner JIHUA 3509 TEXTILE