Glass coated with metal refractive raindrops on surface, and preparation process thereof

A surface coating and preparation process technology, applied in coatings, epoxy resin coatings, etc., can solve problems such as poor adhesion, and achieve the effects of strong adhesion, good shrinkage, and strong water resistance

Active Publication Date: 2021-09-14
YIWU HUAHONG CULTURE CREATIVE CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The present invention aims to overcome the problem of poor adhesion after the existing UV glue shrinks into raindrops, and provides a glass surface coated with metal refraction raindrops and its preparation process. The present invention makes the ring transparent by preparing an epoxy resin composition. The oxygen composition can not only shrink smoothly to form metal refraction raindrops, but also have strong adhesion ability, good scratch resistance and weather resistance, so that metal-like raindrops can be formed on the glass surface, which has a strong artistic decoration effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glass coated with metal refractive raindrops on surface, and preparation process thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] A glass whose surface is coated with metal refraction raindrops comprises a glass plate, the glass plate is provided with an aluminum oxide layer with a thickness of 0.05mm, and the metal refraction raindrops formed by contraction and curing of an epoxy composition are provided on the aluminum oxide layer.

[0043] The preparation process of the glass whose surface is coated with metal refraction raindrops comprises the following preparation steps:

[0044] (1) Clean the glass plate, electroplate the transition layer on the glass surface after cleaning, clean and dry again;

[0045] (2) Add 12.5 parts of brominated bisphenol A type epoxy resin, 10 parts of novolak epoxy resin, 8 parts of triphenylmethane triisocyanate and 9.5 parts of AG-80 four-functional epoxy resin to 12 parts of organic solvent ethylene ethyl alcohol Stir evenly in the glycol ether. After the resin dissolves, an epoxy resin mixture with a viscosity of 4200CPS is obtained. Continue to add 1 part of c...

Embodiment 2

[0049] A glass whose surface is coated with metal refraction raindrops comprises a glass plate, the glass plate is provided with an aluminum oxide layer with a thickness of 0.02 mm, and the metal refraction raindrops formed by shrinking and curing an epoxy composition are provided on the aluminum oxide layer.

[0050] The preparation process of the glass whose surface is coated with metal refraction raindrops comprises the following preparation steps:

[0051] (1) Clean the glass plate, electroplate the transition layer on the glass surface after cleaning, clean and dry again;

[0052] (2) Add 10 parts of brominated bisphenol A epoxy resin, 12 parts of novolac epoxy resin, 5 parts of triphenylmethane triisocyanate and 12 parts of AG-80 tetrafunctional epoxy resin to 8-15 parts of organic solvent Stir evenly in trichlorethylene, and after the resin dissolves, an epoxy resin mixture with a viscosity of 4000CPS is obtained. Continue to add 1.2 parts of curing accelerator salicyli...

Embodiment 3

[0056] A glass whose surface is coated with metal refraction raindrops comprises a glass plate, the glass plate is provided with an aluminum oxide layer with a thickness of 0.08mm, and the metal refraction raindrops formed by shrinking and curing the epoxy composition are provided on the aluminum oxide layer.

[0057] The preparation process of the glass whose surface is coated with metal refraction raindrops comprises the following preparation steps:

[0058] (1) Clean the glass plate, electroplate the transition layer on the glass surface after cleaning, clean and dry again;

[0059] (2) 10 parts of brominated bisphenol A type epoxy resin, 12 parts of novolac epoxy resin, 10 parts of triphenylmethane triisocyanate and 12 parts of AG-80 four-functional epoxy resin are added to 15 parts of organic solvent triethanolamine Stir evenly in the middle, and after the resin dissolves, an epoxy resin mixture with a viscosity of 4500CPS is obtained. Continue to add 1.2 parts of curing ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Viscosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of glass production processes, and concretely relates to a glass coated with metal refraction raindrops on the surface, and a preparation process THEREOF. The glass coated with metal refraction raindrops on the surface comprises a glass plate, a transition layer is arranged on the glass plate, and metal refraction raindrops formed by shrinking and curing an epoxy composition are arranged on the transition layer. The epoxy composition is prepared from, by weight, 10 to 15 parts of brominated bisphenol A type epoxy resin, 8 to 12 parts of novolac epoxy resin, 5 to 10 parts of triphenylmethane triisocyanate, 7 to 12 parts of tetrafunctional epoxy resin, 8 to 15 parts of an organic solvent, 0.8 to 1.2 parts of a curing accelerator and 1 to 1.5 parts of a curing agent. By preparing the epoxy resin composition, the epoxy resin composition can be smoothly shrunk to form metal refraction raindrops, and the raindrops also have relatively strong adhesion ability and relatively good scratch resistance and weather resistance, so that metal-like raindrops are formed on the surface of glass, and a relatively strong artistic decoration effect is achieved.

Description

technical field [0001] The invention relates to the technical field of glass production technology, in particular to a glass whose surface is coated with metal refraction raindrops and a preparation process thereof. Background technique [0002] As we all know, glass is mostly transparent. In order to make the glass have a decorative effect, decorative lines are generally formed on the surface of the glass, but these lines are mostly geometric, linear or frosted. In nature, when raindrops fall on glass or lotus leaves, they will form crystal clear, three-dimensional small water droplets. The metal refraction raindrop is a special effect invented by simulating this natural phenomenon. Existing UV-materials such as coatings and inks with a large shrinkage rate can quickly shrink into the shape of raindrops under the condition of ultraviolet light irradiation, and the large volume shrinkage during the curing process will cause stress and defects that are difficult to eliminate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C17/42C09D163/00C09D163/02C09D163/04
CPCC03C17/42C09D163/00C08L2205/03C08L2205/025C08L63/04C08L63/00
Inventor 龚新明
Owner YIWU HUAHONG CULTURE CREATIVE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com