Preparation method of additive material for replacing composite rock slice and additive material

A technology for adding materials and composite rock flakes, applied in the direction of coating, etc., can solve the problems of poor fusion degree of composite rock flakes, rigid particles in the spraying process, lack of three-dimensional effect, etc., and achieve the effects of simple production equipment, reduced energy consumption, and reduced production costs.

Inactive Publication Date: 2021-10-22
福建格瑞诗化工科技有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention proposes a preparation method and additive material for replacing the additive material of the composite rock slice, which solves the problem of large investment in equipment, high energy consumption, poor fusion of the composite rock slice and lack of three-dimensional effect in the existing composite rock slice production process, and simultaneous spraying The process particles are relatively dull and cannot be spread out

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of additive material for replacing composite rock slice and additive material
  • Preparation method of additive material for replacing composite rock slice and additive material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A method for preparing an additive material for replacing composite rock slices, comprising the steps of:

[0031] S1. Basic paint powder raw material configuration: Take the following raw materials in parts by mass, 1.6-2.4 parts of cellulose, 13.6-20.4 parts of toughening agent, 4-6 parts of titanium dioxide, 8.8-13.2 parts of kaolin, 4-6 parts of lithium magnesium silicate put into the mixer, mix evenly and take out for later use;

[0032] S2. Preparation of base paint: Take 569.7-696.3 parts of deionized water and put them into the dispersion tank, add 1.92-2.88 parts of wetting agent and 1.6-2.4 parts of defoamer in turn, after the dispersion is even, add the prepared base paint in S1 32-48 parts of powder raw materials, 1.2-1.8 parts of pH regulator, 2.8-4.8 parts of bactericide, after strong stirring and dispersion, reduce the speed, add 220.5-269.5 parts of emulsion, 8-12 parts of film-forming aid, and mix well Prepare base paint;

[0033] S3. Preparation of g...

Embodiment 2

[0039] A method for preparing an additive material for replacing composite rock slices, comprising the steps of:

[0040] S1. Basic paint powder raw material configuration: take the following raw materials in parts by mass, 1.8-2.2 parts of cellulose, 15-19 parts of toughening agent, 4.5-5.5 parts of titanium dioxide, 10-12 parts of kaolin, 4.5-5.5 parts of lithium magnesium silicate put into the mixer, mix evenly and take out for later use;

[0041] S2. Preparation of base paint: Take 620-650 parts of deionized water and put it into the dispersion tank, add 2.2-2.6 parts of wetting agent and 1.8-2.2 parts of defoamer in turn, after the dispersion is uniform, add the base paint prepared in S1 38-43 parts of powder raw materials, 1.4-1.7 parts of pH regulator, 3.2-3.7 parts of bactericide, after strong stirring and dispersion, reduce the speed, add 235-256 parts of emulsion, 9-11 parts of film-forming aid, mix well Prepare base paint;

[0042] S3. Preparation of granulation l...

Embodiment 3

[0048] A method for preparing an additive material for replacing composite rock slices, comprising the steps of:

[0049] S1. Basic paint powder raw material configuration: Take the following raw materials in parts by mass, 1.6 parts of cellulose, 13.6 parts of toughening agent, 4 parts of titanium dioxide, 8.8 parts of kaolin, and 4 parts of lithium magnesium silicate, put them into the mixer, and mix them evenly Take out spare;

[0050]S2. Base paint preparation: Take 569.7 parts of deionized water and put it into a dispersion tank, add 1.92 parts of wetting agent and 1.6 parts of defoamer in turn, after the dispersion is uniform, add 32 parts of base paint powder raw materials prepared in S1, pH 1.2 parts of conditioner, 2.8 parts of bactericide, after vigorously stirring and dispersing, reduce the speed, add 220.5 parts of emulsion, 82 parts of film-forming aid, and mix evenly to prepare the base paint;

[0051] S3. Preparation of granulation solution: take 73.6 parts of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a preparation method of an additive material for replacing a composite rock slice and the additive material. The preparation method of the additive material for replacing the composite rock slice comprises the following steps: S1, preparing a basic paint powder raw material; s2, preparing basic paint; s3, preparing granulation liquid; and S4, performing granulation. The prepared additive material has a special spatial three-dimensional structure, and has a higher stone-like effect after being added into the real stone paint; product production equipment is simple, and drying treatment is not needed, so that energy consumption is reduced, and the production cost is reduced; the production process is similar to colorful paint preparation, the operation is simple, and the product consistency is high; and the product has tough particles, and is good in air pressure resistance, smooth in spraying and high in fusion degree among the particles.

Description

technical field [0001] The invention relates to the field of architectural coatings, in particular to a preparation method and the additive material for replacing composite rock slices. Background technique [0002] In recent years, with the improvement of our country's comprehensive strength, people have put forward higher requirements for the living environment, which is comfortable and beautiful at the same time. As a decoration that changes the appearance of the building, the coating is also constantly being updated. Real stone paint as The masterpiece of exterior wall paint naturally needs to incorporate a more realistic imitation stone effect. The introduction of colored sand has successfully changed the single tone of real stone paint. In order to obtain a better imitation stone effect, the research on natural rock flakes and composite rock flakes has now begun. , crushed, the production process requires a lot of equipment investment, high energy consumption, poor fu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D7/61C09D7/65
CPCC09D7/61C09D7/65
Inventor 林景琼林景奎杨智明
Owner 福建格瑞诗化工科技有限公司