Compound hydroxyl diguanide tetrafluoride triborate, hydroxyl diguanide tetrafluoride triborate nonlinear optical crystal, preparation methods of compound hydroxyl diguanide tetrafluoride triborate and hydroxyl diguanide tetrafluoride triborate nonlinear optical crystaland application of hydroxyl diguanide tetrafluoride triborate nonlinear optical crystal
A technology of diguanidine hydroxytetrafluorotriborate and hydroxytetrafluorotriboric acid, which is applied in the fields of nonlinear optics, preparation of organic compounds, organic chemical methods, etc., can solve the difficulty of large-sized crystals, small birefringence, and limited Application and other issues, to achieve the effect of low cost, easy large-size crystals, and fast growth
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0047] Preparation compound:
[0048] According to the reaction formula: 2[C(NH 2 ) 3 ]HF 2 +3H 3 BO 3 →[C(NH 2 ) 3 ] 2 [B 3 o 3 f 4 (OH)]+5H 2 O, using the evaporation method to synthesize the compound [C(NH 2 ) 3 ] 2 [B 3 o 3 f 4 (OH)]:
[0049] a. [C(NH 2 ) 3 ]HF 2 、H 3 BO 3 Mix evenly at a molar ratio of 2:3 to obtain a mixed solution,
[0050] b. Transfer the mixed solution in step a into a polytetrafluoroethylene beaker with a volume of 50mL, raise the temperature to 50°C at a rate of 10°C / h, and let it stand at a constant temperature for 2 days. Quickly clean the product in the polytetrafluoroethylene lining, and dry it at room temperature to obtain the compound [C(NH 2 ) 3 ] 2 [B 3 o 3 f 4 (OH)];
Embodiment 2
[0052] Preparation compound:
[0053] According to the reaction formula: 2[C(NH 2 ) 3 ]NO 3 +3H 3 BO 3 +2RbHF 2 →[C(NH 2 ) 3 ] 2 [B 3 o 3 f 4 (OH)]+5H 2 O+2RbNO 3 , the compound [C(NH2 ) 3 ] 2 [B 3 o 3 f 4 (OH)]:
[0054] a. [C(NH 2 ) 3 ]NO 3 、H 3 BO 3 , RbHF 2 Mix evenly in a molar ratio of 2:3:2, add 50mL of deionized water to fully mix and dissolve to obtain a mixed solution,
[0055] b. Transfer the mixed solution in step a into a polytetrafluoroethylene beaker with a volume of 80mL, raise the temperature to 40°C at a rate of 15°C / h, and let it stand at a constant temperature for 3 days. Quickly clean the product in the polytetrafluoroethylene lining, and dry it at room temperature to obtain the compound [C(NH 2 ) 3 ] 2 [B 3 o 3 f 4 (OH)];
Embodiment 3
[0057] Preparation compound:
[0058] According to the reaction formula: 2[C(NH 2 ) 3 ]NO 3 +3H 3 BO 3 +2CsHF 2 →[C(NH 2 ) 3 ] 2 [B 3 o 3 f 4 (OH)]+5H 2 O+2CsNO 3 , the compound [C(NH 2 ) 3 ] 2 [B 3 o 3 f 4 (OH)]:
[0059] a. [C(NH 2 ) 3 ]NO 3 、H 3 BO 3 , CsHF 2 Mix evenly at a molar ratio of 2:3:2, add 10 mL of deionized water to fully mix and dissolve to obtain a mixed solution,
[0060] b. Transfer the mixed solution in step a into a polytetrafluoroethylene beaker with a volume of 100mL, raise the temperature to 45°C at a rate of 20°C / h, and let it stand at constant temperature for 4 days. Quickly clean the product in the polytetrafluoroethylene lining, and dry it at room temperature to obtain the compound [C(NH 2 ) 3 ] 2 [B 3 o 3 f 4 (OH)];
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap