Method for evaluating aging degree of silicone rubber through inorganic degree

An aging degree, silicone rubber technology, applied in the direction of material analysis, measuring devices, instruments, etc. by optical means, can solve the problems of immaturity, surface hydrophobicity, decreased mechanical properties, inability to meet the actual needs of on-site inspection, and achieve operation Simple, objective and reliable results

Pending Publication Date: 2021-12-10
JIANGSU SHENMA ELECTRIC CO LTD
View PDF5 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Inorganic silicidation will directly lead to the decrease of surface hydrophobicity and mechanical properties, so that the safety of product operation cannot be guaranteed
[0003] For the evaluation method of the degree of inorganicization, X-ray diffraction energy spectroscopy (XPS) is mainly used to characterize it at present, but the XPS detection time is long and the detection requirements are high, which cannot meet the actual needs of on-site detection. It can be said that silicone rubber products are inorganic The standardized evaluation system is immature, it is necessary to study new methods and apply them

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for evaluating aging degree of silicone rubber through inorganic degree
  • Method for evaluating aging degree of silicone rubber through inorganic degree
  • Method for evaluating aging degree of silicone rubber through inorganic degree

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0025] As required, specific embodiments of the invention will be disclosed herein. However, it should be understood that the embodiments disclosed herein are merely typical examples of the invention, which can be embodied in various forms. Therefore, specific details disclosed herein are not to be considered limiting, but merely as a basis for the claims and as a representative basis for teaching one skilled in the art to variously employ the invention in any appropriate way in practice, This includes taking various features disclosed herein and combining features that may not be expressly disclosed herein.

[0026] Such as figure 1 As shown, an embodiment of the present invention provides a method for evaluating the degree of aging of silicone rubber through the degree of inorganicization, comprising the following steps,

[0027] Step 1: Select the silicone rubber product to be tested as the test sample, and select inorganic SiO 2 as a control sample.

[0028] Step 2: Us...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for evaluating the aging degree of silicone rubber through the inorganic degree, wherein the method comprises the following steps: 1, selecting a silicone rubber product to be tested as a test sample, and selecting inorganic SiO2 as a control sample; 2, carrying out infrared spectrum characterization on the test surface of the test sample and the surface of the control sample by using an infrared spectrometer to obtain an infrared characteristic spectrogram of Si-O-Si of the test sample and an infrared characteristic spectrogram of inorganic SiO2; and step 3, judging the inorganic degree of the silicone rubber product according to the displacement difference of the infrared characteristic peak of Si-O-Si relative to the infrared characteristic peak of inorganic SiO2 on the wave number, and further evaluating the aging degree of the silicone rubber product through the inorganic degree. According to the method, the surface inorganic degree of the silicone rubber product is represented by the infrared spectrometer, the aging degree of the silicone rubber product is evaluated through the inorganic degree, the operation is simple, the result can be obtained through simple subtraction formula calculation, and the result is objective and reliable.

Description

technical field [0001] The invention relates to the technical field of high-voltage insulation detection, in particular to a method for evaluating the aging degree of silicone rubber through the degree of inorganicization. Background technique [0002] Silicone rubber products have the advantages of light weight, good stain resistance, and convenient maintenance, and are widely used in the field of high-voltage insulation. But since silicone rubber is a class of -CH 3 For polymer materials with side chains and Si-O-Si main chains, under the joint action of high temperature, ultraviolet light, humidity and other conditions, the main and side chains will inevitably break and age. Aging will be accompanied by many aging characteristics, such as decreased elongation at break, increased hardness, inorganic siliconization, etc., among which inorganic siliconization is one of the important characteristics in the aging process. Inorganic silicidation will directly lead to the decr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): G01N21/3563
CPCG01N21/3563
Inventor 张林军夏超楠孙名伟陈文静刘超张鑫鑫
Owner JIANGSU SHENMA ELECTRIC CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com