Method for preparing slurry suitable for automatic grouting line of wine bottle

An automatic grouting and wine bottle technology, which is applied to clay products, applications, household appliances, etc., can solve the problems of large shrinkage fluctuations, poor stability, adjustability and strain resistance, and excessive bottleneck size, so as to achieve easy adjustment and water repellency good sex effect

Pending Publication Date: 2022-02-25
合江县华艺陶瓷制品有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The traditional mud should be mechanized and automated, with poor stability, adjustability and strain, especially the fluctuation of slurry suction time, which often exceeds the speed setting range of the grouting machine
Large fluctuations in shrinkage, resulting in precisely controlled bottlenecks that are often oversized and do not fit the cap

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing slurry suitable for automatic grouting line of wine bottle
  • Method for preparing slurry suitable for automatic grouting line of wine bottle
  • Method for preparing slurry suitable for automatic grouting line of wine bottle

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A kind of slurry suitable for wine bottle automatic grouting line, said slurry suitable for wine bottle automatic grouting line includes ball abrasive and chemical slurry;

[0033] The ball milling material includes ball milling raw materials, ball stones and ball milling water, and the ratio of the ball milling raw materials, ball stones and ball milling water is 1:1.5:1;

[0034] The ball milling raw material includes the following components in parts by weight:

[0035]

[0036] Described pulping material comprises pulping raw material and pulping water, and the ratio of described pulping raw material and pulping water is 7:3;

[0037] The pulping raw material comprises the following components by weight:

[0038] 19 parts by weight of washed kaolin from Zhangzhou, Fujian;

[0039] 19 parts by weight of Inner Mongolia washed kaolin.

[0040] The parts by weight of the plasticizer can be adjusted by increasing the plasticizer by 0.5-1 part by weight or reducing ...

Embodiment 2

[0072] A kind of slurry suitable for wine bottle automatic grouting line, said slurry suitable for wine bottle automatic grouting line includes ball abrasive and chemical slurry;

[0073] The ball milling material includes ball milling raw materials, ball stones and ball milling water, and the ratio of the ball milling raw materials, ball stones and ball milling water is 1:1.5:1;

[0074] The ball milling raw material includes the following components in parts by weight:

[0075]

[0076] Described pulping material comprises pulping raw material and pulping water, and the ratio of described pulping raw material and pulping water is 7:3;

[0077] The pulping raw material comprises the following components by weight:

[0078] 23 parts by weight of washed kaolin from Zhangzhou, Fujian;

[0079] 23 parts by weight of Inner Mongolia washed kaolin.

[0080] The parts by weight of the plasticizer can be adjusted by increasing the plasticizer by 0.5-1 part by weight or reducing ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing slurry suitable for an automatic grouting line of a wine bottle. The method comprises the following steps: S1, carrying out ball milling operation on a ball milling material, and carrying out ball milling detection to obtain a qualified mixture; wherein the ball-milling material comprises a ball-milling raw material, ballstone and ball-milling water; the ball-milling raw materials comprise Hubei jade potassium feldspar, Anhui Fengyang quartz, Zhangzhou black clay, a plasticizer and dolomite; S2, slurrying the slurry to obtain slurried kaolin; wherein the slurry comprises slurrying raw materials and slurrying water; the slurry raw materials comprise Zhangzhou washed kaolin in Fujian and Inner Mongolia washed kaolin; S3, mixing the mixture which is detected to be qualified with the slurried kaolin, and squeezing to obtain a mud cake; and S4, dividing the mud cake in the step S3 into two parts, wherein one part of the mud cake is used for production of an automatic grouting machine after being subjected to slurrying and aging operation, and the other part of the mud cake is used for rolling the bottleneck after being subjected to pugging and aging operation. The prepared slurry is suitable for production of an automatic grouting machine.

Description

technical field [0001] The invention relates to the field of wine bottle manufacturing, in particular to a method for preparing slurry suitable for an automatic grouting line for wine bottles. Background technique [0002] Since ancient times, the daily-use ceramics industry has been dominated by manual operations, with low efficiency, especially in the molding process, basically relying on more people to increase production, because of the influence of human factors, the pass rate is low, and zero-defect wine bottles The average pass rate of products hovers below 65%. If mechanization and automatic production are used, it is difficult to prepare suitable mud. Therefore, high-quality and stable mud is the key to automation and the core element of stable quality for ceramic manufacturers. [0003] The traditional mud should be mechanized and automated, with poor stability, adjustability and strain, especially the fluctuation of slurry suction time, which often exceeds the s...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/04C04B33/13C04B33/24C04B33/28
CPCC04B33/04C04B33/13C04B33/1305C04B33/131C04B33/28C04B33/24C04B2235/3472C04B2235/3418C04B2235/442
Inventor 肖书明
Owner 合江县华艺陶瓷制品有限公司