Ultra-black cotton-like silk and processing method thereof

A processing method and technology of imitating cotton, applied in the manufacture of rayon, single-component polyester rayon, chemical characteristics of fibers, etc., can solve problems such as poor color fastness, improve color fastness and improve anti-aging performance , Improve the effect of color blackness

Pending Publication Date: 2022-03-11
福建百宏聚纤科技实业有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most of the existing ultra-black imitation cotton silks are printed and dyed onto polyester fibers through printing and dyeing processing to achieve a black effect, but the color fastness is not good

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] A kind of processing method of ultra-black imitation cotton silk, this processing method comprises the following steps:

[0020] (1) Esterification of phthalic acid, ethylene glycol and isophthalic acid for 2.5 hours to obtain mixture A;

[0021] (2) Add antioxidant, matting agent, color masterbatch and antibacterial agent to mixture A to obtain modified polyester slices; wherein, after adding antioxidant, matting agent, color masterbatch and antibacterial agent, heat up to 250°C and vacuumize, Heat up to 265°C and continue vacuuming, then discharge when the melt viscosity is 0.75dl / g, and obtain modified polyester chips; the color masterbatch includes the following raw materials in weight percentages: carbon black 0.4%, polyester chips 94.2%; wherein, The specific preparation process of color masterbatch is: firstly weigh the raw material carbon black and polyester slices required for the production of color masterbatch, then grind the carbon black and polyester slices...

Embodiment 2

[0027] A kind of processing method of ultra-black imitation cotton silk, this processing method comprises the following steps:

[0028] (1) Esterification of phthalic acid, ethylene glycol and isophthalic acid for 2.8 hours to obtain mixture A;

[0029] (2) Add antioxidant, matting agent, color masterbatch and antibacterial agent to mixture A to obtain modified polyester slices; wherein, after adding antioxidant, matting agent, color masterbatch and antibacterial agent, heat up to 255 ° C and vacuumize, Raise the temperature to 270°C and continue vacuuming, and then discharge when the melt viscosity is 0.76dl / g to obtain modified polyester chips; the masterbatch includes the following raw materials in weight percentages: carbon black 3.1%, polyester chips 97.6%; among them, The specific preparation process of color masterbatch is: firstly weigh the raw material carbon black and polyester slices required for the production of color masterbatch, then grind the carbon black and p...

Embodiment 3

[0035] A kind of processing method of ultra-black imitation cotton silk, this processing method comprises the following steps:

[0036] (1) Esterification of phthalic acid, ethylene glycol and isophthalic acid for 3 hours to obtain mixture A;

[0037] (2) Add antioxidant, matting agent, color masterbatch and antibacterial agent to mixture A to obtain modified polyester slices; wherein, after adding antioxidant, matting agent, color masterbatch and antibacterial agent, heat up to 260°C and vacuumize, Raise the temperature to 275°C and continue vacuuming, and then discharge when the melt viscosity is 0.78dl / g to obtain modified polyester chips; the color masterbatch includes the following raw materials in weight percentages: carbon black 5.8%, polyester chips 99.6%; among them, The specific preparation process of color masterbatch is: firstly weigh the raw material carbon black and polyester slices required for the production of color masterbatch, then grind the carbon black and...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a processing method of ultra-black imitation cotton silk, which comprises the following steps: carrying out esterification reaction on phthalic acid, ethylene glycol and isophthalic acid to obtain a mixture A; adding an antioxidant, a delustering agent, color master batches and an antibacterial agent into the mixture A to obtain modified polyester chips; wherein the color master batch is prepared from the following raw materials in percentage by weight: 0.4 to 5.8 percent of carbon black and 94.2 to 99.6 percent of polyester chips; the modified polyester slices are dried through a rotary drum and then extruded through double screws for melt spinning, and the super-black cotton-like silk is obtained.

Description

technical field [0001] The invention relates to the technical field of fiber preparation, in particular to an ultra-black imitation cotton silk and a processing method thereof. Background technique [0002] Super-imitation cotton products are not only similar to cotton fabrics in terms of fiber surface shape and fabric design style, but more importantly, their fabric characteristics and functions are cotton-like and super-cotton, and have high-quality dynamic moisture comfort performance. Super imitation cotton can well make up for the defects of cotton fibers, and use the characteristics of polyester to make up for the shortage of fibers, and the fabric made has improved durability. Most of the existing ultra-black imitation cotton silks are printed and dyed black on the polyester fiber by printing and dyeing processing to achieve the black effect, but the color fastness is not good. Contents of the invention [0003] In view of the above problems, the invention provides...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D01F6/92D01F1/10C08G63/183C08G63/181
CPCD01F6/92D01F1/10D01F1/103C08G63/183C08G63/181
Inventor 刘智敏陈阿斌鲁传旺
Owner 福建百宏聚纤科技实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com