High-performance rotational molding product cross-linking foaming molding process
A molding process and high-performance technology, which is applied in the field of cross-linking foam molding of high-performance rotomolding products to achieve the effects of strong impact resistance, high plasticity and easy operation.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0014] Example 1
[0015] A cross-linking foaming process of high performance rolled articles, including the following steps:
[0016] S1, the mold selection, select the desired mold, the internal formation of the material is placed, and the upper portion is open, and the mold is fixed in the heating chamber.
[0017] S2, the plastic sheet is pulverized with a grinder, ground to plastic powder, spare, and plastic powder to 20 mesh.
[0018] S3, in introducing the plastic powder in S2 into the material placement space in the mold in S1, the mold, the mold peripheral wall is fixed, and the upper portion of the mold is opened.
[0019] S4, adding a stabilizer and a catalyst to the inlet slot in the upper portion of the upper portion of S1 to 40 ° C, S3, and the catalyst is an alkali metal compound, and the stabilizer is hydroxybenzophenone, and the mixer is stirred, the mixer The rotational speed is 10R / min, until the stabilizer and the catalyst are completely fused with the plasti...
Example Embodiment
[0022] Example 2
[0023] A cross-linking foaming process of high performance rolled articles, including the following steps:
[0024] S1, the mold selection, select the desired mold, the internal formation of the material is placed, and the upper portion is open, and the mold is fixed in the heating chamber.
[0025] S2, the plastic sheet is pulverized with a grinder, ground to plastic powder, spare, and plastic powder to 50 mesh.
[0026] S3, in introducing the plastic powder in S2 into the material placement space in the mold in S1, the mold, the mold peripheral wall is fixed, and the upper portion of the mold is opened.
[0027] S4, adding stabilizers and catalysts to the inlet slot of the heating indoor temperature in S1 to 45 ° C, S3, and the catalyst, the catalyst is an alkali metal compound, the stabilizer is hydroxybenzophenone, stirring, stirring, mixer The rotational speed is 13R / min, until the stabilizer and the catalyst are completely fused to the plastic powder, an...
Example Embodiment
[0030] Example 3
[0031] A cross-linking foaming process of high performance rolled articles, including the following steps:
[0032] S1, the mold selection, select the desired mold, the internal formation of the material is placed, and the upper portion is open, and the mold is fixed in the heating chamber.
[0033] S2, the plastic sheet is pulverized with a grinder, ground to plastic powder, spare, and plastic powder to 80 mesh.
[0034] S3, in introducing the plastic powder in S2 into the material placement space in the mold in S1, the mold, the mold peripheral wall is fixed, and the upper portion of the mold is opened.
[0035] S4, adding a stabilizer and a catalyst to the inlet groove of the heating indoor temperature in S1 to 50 ° C, S3, and the catalyst is added to the catalyst, the catalyst is an alkali metal compound, and the stabilizer is hydroxybenzophenone, and the mixer is stirred, the mixer The rotational speed is 16R / min until the stabilizer and the catalyst are ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap