Anti-pilling multifunctional biomass yarn and preparation method thereof

A multi-functional, biomass technology, applied in the field of textile yarn, can solve the problems of easy pilling and neck jamming

Pending Publication Date: 2022-05-10
JIANGSU NADN SCI TECH CO LTD +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the problems existing in the prior art, the present invention provides an anti-pilling multifunctional biomass yarn and a preparation method thereof. The biomass yarn solves the neck problem that polyester and cellulose fiber blended yarns are prone to pilling, Obtain blended yarns with good pilling resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-pilling multifunctional biomass yarn and preparation method thereof
  • Anti-pilling multifunctional biomass yarn and preparation method thereof
  • Anti-pilling multifunctional biomass yarn and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] The present invention first provides an anti-pilling multi-functional biomass yarn, which is a yarn obtained by blending multi-functional polyester fibers and biomass viscose fibers in a mass ratio of 35:65. Among them, the multifunctional polyester fiber is an antibacterial multifunctional polyester fiber with an accordion groove surface, specifically GENOMEX fiber. GENOMEX fiber is provided by Jiangsu Nadun Technology Co., Ltd.

[0026] The present invention also provides a method for preparing the above-mentioned anti-pilling multifunctional biomass yarn, which includes the following steps: mixing the antibacterial, hygroscopic and quick-drying polyester GENOMEX fiber with the surface of the accordion pleat groove to the biomass viscose fiber in a mass ratio of 35:65 Carry out layered iterative laying and mixing (2 layers of polyester and 2 layers of viscose), drawn into tops, and then input to the vortex spinning machine for spinning, the yarn specification is contr...

Embodiment 2

[0029] The present invention first provides an anti-pilling multi-functional biomass yarn, which is a yarn obtained by blending multi-functional polyester fibers and biomass cotton fibers in a mass ratio of 40:60. Among them, the multifunctional polyester fiber is an antibacterial multifunctional polyester fiber with an accordion groove surface, specifically GENOMEX fiber. GENOMEX fiber is provided by Jiangsu Nadun Technology Co., Ltd.

[0030] The present invention also provides a method for preparing the above-mentioned anti-pilling multifunctional biomass yarn, which includes the following steps: mixing the antibacterial, moisture-absorbing and quick-drying polyester GENOMEX fibers with the surface of the accordion pleats and the biomass cotton fibers in a mass ratio of 40:60. Layered iteratively laying mix (3 layers of polyester and 2 layers of cotton), drawn into tops, and then input to the vortex spinning machine for spinning, the yarn specification is controlled at 40S,...

Embodiment 3

[0032] The invention first provides an anti-pilling multifunctional biomass yarn, which is a yarn that is blended with multifunctional polyester fibers, biomass cotton, and biomass viscose fibers in a mass ratio of 40:30:30 . Among them, the multifunctional polyester fiber is an antibacterial multifunctional polyester fiber with an accordion groove surface, specifically GENOMEX fiber. GENOMEX fiber is provided by Jiangsu Nadun Technology Co., Ltd.

[0033] The present invention also provides a method for preparing the above-mentioned anti-pilling multifunctional biomass yarn, which includes the following steps: combining the antibacterial, moisture-absorbing and quick-drying polyester GENOMEX fiber with the surface of the accordion pleat groove with the biomass cotton and the biomass viscose mixed fiber according to 40 : 30:30 mass ratio for layered iterative laying and mixing (3 layers of polyester, 1 layer of cotton, 1 layer of viscose), drawn into tops, and then input to t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an anti-pilling multifunctional biomass yarn and a preparation method thereof, and the method comprises the following steps: mixing biomass cellulose fibers and polyester fibers according to layered iteration lapping, drawing into wool tops, then inputting into a vortex spinning machine for spinning, and controlling the yarn specification to be 21S-60S. According to the anti-pilling multifunctional biomass yarn prepared through the method, the antibacterial property, the quick-drying property and the fiber strength of the yarn are guaranteed through the antibacterial multifunctional polyester fibers with the organ pleat groove surfaces, and the moisture absorption and the skin-friendly property of the yarn are guaranteed through the biomass cellulose fibers; the groove surface of the organ pleat and the kidney-shaped structure of the biomass cellulose fiber are effectively engaged in a vortex spinning machine, the special combination solves the neck clamping problem that the polyester and biomass cellulose fiber blended yarn is prone to pilling, the blended yarn good in pilling resistance is obtained, meanwhile, the blended yarn is endowed with multiple functions such as antibiosis, moisture absorption and quick drying, and the anti-pilling effect is good. The fabric can be widely applied to the fields of clothes and home textiles, especially textiles in direct contact with human skin.

Description

technical field [0001] The invention relates to the field of textile yarns, in particular to an anti-pilling multifunctional biomass yarn and a preparation method thereof. Background technique [0002] China is a big textile country. 70% of the world's chemical fibers come from China, of which polyester accounts for 70% of the chemical fibers. However, polyester has been only used for cheap commodities because of its lack of water absorption, airtightness, and easy generation of static electricity, especially when mixed with viscose and cotton. It is easy to pilling later, which is the bottleneck of the industry. How to solve this problem is the technical barrier to whether polyester can be high-end. SUMMARY OF THE INVENTION [0003] In order to solve the problems existing in the prior art, the present invention provides an anti-pilling multifunctional biomass yarn and a preparation method thereof. The biomass yarn solves the problem of easy pilling of polyester and cellul...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D02G3/04D01D5/253D01F1/10D01H4/02D06B1/00
CPCD02G3/045D02G3/04D01D5/253D01F1/10D01H4/02D06B1/00
Inventor 郑敏王作山
Owner JIANGSU NADN SCI TECH CO LTD