Compression-resistant water permeable brick and preparation method thereof

A technology of permeable bricks and permeable concrete, applied in auxiliary forming equipment, ceramic products, manufacturing tools, etc., can solve problems affecting the smoothness of the road surface, broken permeable bricks, and lack of anti-segregation, etc., to improve the compressive capacity and prolong the service life The effect of improving the lifespan and improving the overall quality

Pending Publication Date: 2022-06-21
张磊
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] 1. The existing permeable bricks do not have high-efficiency compression resistance. If a large vehicle drives on the road formed by the permeable bricks, it will easily cause the permeable bricks to break and affect the smoothness of the road surface;
[0004] 2. During the production of permeable bricks, concrete storage tanks are required to temporarily store permeable concrete. The existing concrete storage tanks do not have the function of preventing segregation. After a period of time, permeable concrete will segregate, which will affect the overall performance of permeable bricks. quality

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Compression-resistant water permeable brick and preparation method thereof
  • Compression-resistant water permeable brick and preparation method thereof
  • Compression-resistant water permeable brick and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] First, as Figure 1-9 As shown, the present invention provides a compression-resistant permeable brick, the compression-resistant permeable brick includes a compression-resistant frame body 1, and the top of the compression-resistant frame body 1 is provided with a honeycomb vertical water-permeable groove 11. Both the front and the back are provided with horizontal permeable grooves 12. Through the preparation of the compression-resistant frame body 1, the permeable concrete can be framed and supported. With the design of the honeycomb vertical permeable grooves 11 and horizontal water permeable grooves 12, it is possible to ensure the water permeability of the permeable concrete. On the premise, improve the compressive capacity of pervious concrete.

Embodiment 2

[0046] Second, as Figure 1-9 As shown, the present invention provides a preparation method of a compression-resistant permeable brick, and the preparation method of the compression-resistant permeable brick comprises the following steps:

[0047] S1, the preparation of the compression frame, specifically:

[0048] Step A1, the compression-resistant frame body includes the following raw material components in parts by weight: 36-45 parts of red shale, 20-32 parts of sodium montmorillonite, 18-30 parts of glass sand, 13-22 parts of fly ash and 8-15 parts of yellow mud, the raw materials for preparing the compression-resistant frame are added to the ball mill in turn, and the ball mill is controlled to grind it. During the grinding process, water is added in the proportion of 1.5%, and then the frame with a soft texture can be processed. raw material;

[0049] Step A2, adding the above-mentioned frame body raw materials to the interior of the frame body mold, then using a pres...

Embodiment 3

[0053] like Figure 1-9 As shown, on the basis of Embodiment 2, the present invention provides a technical solution: preferably, the concrete storage tank includes a thermal insulation tank body 2, and a support frame 21 is fixedly welded on the outer wall of the thermal insulation tank body 2. The inner cavity is provided with an anti-segregation mechanism 3, the bottom of the thermal insulation tank 2 is provided with a quantitative output mechanism 4, the top of the thermal insulation tank 2 is provided with a large particle removal mechanism 5, and the anti-segregation mechanism 3 includes a drive motor 31 and a hollow disk 32, The driving motor 31 is fixedly installed on the top of the thermal insulation tank 2, the hollow disk 32 is fixedly mounted on the top of the inner cavity of the thermal insulation tank 2, the bottom of the hollow disk 32 is fixedly connected with a vertical pipe 33, and the output shaft of the driving motor 31 extends to the hollow The inner cavit...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a compression-resistant water permeable brick and a preparation method thereof, and relates to the technical field of concrete brick preparation, the compression-resistant water permeable brick comprises a compression-resistant frame body, honeycomb vertical water permeable grooves are formed in the top of the compression-resistant frame body, and horizontal water permeable grooves are formed in the front and back of the compression-resistant frame body; the preparation method of the compression-resistant water permeable brick comprises the following steps: S1, preparing the compression-resistant frame body; s2, preparation of pervious concrete; and S3, final treatment of the water permeable brick. The step S1 further comprises the following steps: step A1, the compression-resistant frame body comprises the following raw material components in parts by weight: 36-45 parts of red shale, 20-32 parts of Na-montmorillonite and the like. Through preparation of the compression-resistant frame body, frame support can be performed on the pervious concrete, and the design of honeycomb vertical pervious grooves and horizontal pervious grooves is matched, so that on the premise of ensuring the water permeability of the pervious concrete, the compression-resistant capability of the pervious concrete is improved, and the problem that the pervious bricks are easily broken due to extrusion of large vehicles is avoided; the service life of the water permeable brick is prolonged.

Description

technical field [0001] The invention relates to the technical field of concrete brick preparation, in particular to a compression-resistant permeable brick and a preparation method thereof. Background technique [0002] Permeable concrete is a type of concrete developed and used for the defects of urban road pavement, which can allow rainwater to flow into the ground to effectively replenish groundwater. It can effectively alleviate urban environmental problems such as a sharp drop in urban groundwater levels, and can effectively eliminate oil compounds on the ground. Harmful to environmental pollution, permeable concrete, as an excellent pavement material that can effectively protect groundwater, maintain ecological balance, and alleviate urban heat island effect, is usually made into permeable concrete bricks and popularized in many countries. The following problems exist for the prior art: [0003] 1. The existing permeable bricks do not have high-efficiency compressive ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E01C5/06E01C11/22C04B28/00C04B28/04C04B38/00B28B3/02B28B17/02B28B11/24
CPCE01C5/06E01C5/065E01C11/225C04B28/001C04B28/04B28B3/02B28B17/026B28B11/245E01C2201/20C04B2111/00284C04B14/108C04B14/22C04B18/08C04B14/361C04B14/048C04B18/146C04B18/0436C04B2103/0045C04B38/00
Inventor 张磊
Owner 张磊