Reusable traceless strong daub and preparation method thereof

A technology of superglue and mastic, applied in adhesives, non-polymer adhesive additives, adhesive additives, etc., can solve the problems of high cost, difficult to remove completely, and large rubber usage, and achieve simple preparation methods and excellent ductility Sexuality and low cost effect

Active Publication Date: 2022-07-29
杭州延一电子商务有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the cement produced by using this raw material is too hard, and it is easy to remain on the wall surface during use and it is difficult to remove completely. At the same time, the amount of rubber used in the production process is large and the cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Reusable traceless strong daub and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A kind of reusable non-marking strong mastic of the present embodiment, the mastic comprises the following raw materials:

[0033] Phase A: cis-1,4-polybutadiene rubber 300g, 7# mechanical oil 350g and calcium carbonate 1800g;

[0034] Phase B: 1066# chlorobutyl rubber 1000g;

[0035] Phase C: 14500 g of calcium carbonate and 2300 g of polyisobutylene.

[0036] The preparation method of the reusable non-marking super glue of the present embodiment comprises the following steps:

[0037] (1) according to the weight of each raw material, respectively take by weighing for subsequent use;

[0038] (2) Mix phase A and phase B in an open rubber mixing machine for 15 minutes. During the mixing process, a polymer chemical reaction occurs, exothermic, and the open rubber mixing machine is controlled to ensure complete reaction until no foaming occurs, and a mixture is obtained. A;

[0039] (3) continue mixing described mixture A in the rubber mixer for 8min, then add phase C...

Embodiment 2

[0042] A kind of reusable non-marking strong mastic of the present embodiment, the mastic comprises the following raw materials:

[0043] Phase A: cis-1,4-polybutadiene rubber 340g, 7# machine oil 300g and calcium carbonate 2000g;

[0044] Phase B: 1066# chlorinated butyl rubber 1200g;

[0045] Phase C: 15000 g of calcium carbonate and 2500 g of polyisobutylene.

[0046] The preparation method of the reusable non-marking super glue of the present embodiment comprises the following steps:

[0047] (1) according to the weight of each raw material, respectively take by weighing for subsequent use;

[0048] (2) Mix phase A and phase B in an open rubber mixer for 20 minutes. During the mixing process, a polymer chemical reaction occurs, exothermic, and the open rubber mixer is controlled to ensure complete reaction until no foaming occurs, and a mixture is obtained. A;

[0049] (3) continue mixing 10min of described mixture A in rubber mixer, add C phase and mix 20min again, ob...

Embodiment 3

[0052] A kind of reusable non-marking strong mastic of the present embodiment, the mastic comprises the following raw materials:

[0053] Phase A: cis-1,4-polybutadiene rubber 380g, 7# machine oil 250g and calcium carbonate 2200g;

[0054] Phase B: 1066# chlorinated butyl rubber 1400g;

[0055] Phase C: 15500 g of calcium carbonate and 2700 g of polyisobutylene.

[0056] The preparation method of the reusable non-marking super glue of the present embodiment comprises the following steps:

[0057] (1) according to the weight of each raw material, respectively take by weighing for subsequent use;

[0058] (2) Mix phase A and phase B in an open rubber mixer for 25 minutes. During the mixing process, a polymer chemical reaction occurs, exothermic, and the open rubber mixer is controlled to ensure that the reaction is complete until no foaming occurs, and a mixture is obtained. A;

[0059] (3) continue mixing described mixture A in the rubber mixing machine for 12min, then add ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to reusable traceless strong daub and a preparation method thereof, and the daub is prepared from the following raw materials: a phase A: cis-1, 4-polybutadiene rubber, machine oil and calcium carbonate; a phase B: chlorinated butyl rubber; and phase C: calcium carbonate and polyisobutene. According to the reusable traceless strong daub, through the synergistic effect of the raw materials, the reusable traceless strong daub has excellent ductility and viscidity, a consumer can rub a mixture conveniently, the reusable traceless strong daub is applied to an adherend, the reusable traceless strong daub can be reused, no residual trace exists after the reusable traceless strong daub is taken down, the preparation method of the daub is simple, large-scale production can be achieved, and the cost is low.

Description

technical field [0001] The invention belongs to the technical field of viscose, and in particular relates to a reusable traceless strong glue and a preparation method thereof. Background technique [0002] In the field of household adhesives, there is a general need to stick but also need to remove the adherend. Such as decorative balloons used at parties, small photo frames hanging on the wall at home, and post-it notes for daily notes. The traditional adhesive that solves the need for pasting generally leaves traces on the surface of the adherend, and the adhesive cannot be reused. [0003] At the same time, in the field of nail art, a new manicurist needs to practice different nail pieces repeatedly, and needs to install different decorative pieces on the nail plate, but it needs to be removed after practice. The existing general viscose preparations are difficult to meet the repetition Use, no residue needs. Nail art users also need manicure decorations that can be re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J123/22C09J11/04C09J11/08
CPCC09J123/22C09J11/04C09J11/08C08K2003/265C08L9/00C08L91/00C08L23/283C08K3/26Y02W30/91
Inventor 柴鑫玉
Owner 杭州延一电子商务有限公司