Environment protection type water permeable brick

A permeable brick, an environmentally friendly technology, applied to clay products, pavements paved with prefabricated blocks, roads, etc., can solve problems such as poor water permeability, urban environmental protection, harmful plant protection, increase urban heat island effect, etc., and achieve good water permeability , Solve supplementary problems, carrying capacity anti-slip effect

Inactive Publication Date: 2004-10-06
曹正茂
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] 1. Due to its extremely poor water permeability, it directly blocks the infiltration of rainwater. As a result, the urban groundwater source cannot be replenished, which aggravates the drought phenomenon in the city;
[0004] 2. The reflection of sunlight on the road greatly increases the urban heat island effect;
[0005] 3. It is extremely harmful to the environmental protection and plant protection of the urban area, and directly affects the growth of flowers and trees

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] a, getting particle size by weight is 80% of 15 purpose bauxite pellets (will contain AI 2 o 3 70%-80% of bauxite is crushed by a crusher and a pair of rollers, and then screened by a vibrating sieve), 7% of 250-300 mesh clay fine powder, 6% of talcum powder, and 7% of bentonite. 5%-8% water by weight is fully stirred for about 30 minutes;

[0015] b. Put the stirred mixture into the mold and carry out vibration molding under the pressure condition of 500-800 tons, and the time is controlled within 10-15 seconds;

[0016] c. Send the shaped bricks into the drying room for drying:

[0017] d. Carry out kiln calcination for the dried brick adobe, the temperature is controlled between 1250-1280°C, and it is enough to keep it for 100-120 minutes.

[0018] The product that the present embodiment produces is the common floor tile without color.

Embodiment 2

[0020] a. Take the bauxite powder with a particle size of 300 mesh by weight and add 90%-96% of bauxite powder with 4%-8% grass green dye additive, add the water of 4%-8% of the above-mentioned total weight and carry out sufficient stirring. After mixing, add Molding, drying and calcining according to the traditional process, and then crushing to make grass green bauxite pellets of about 20 meshes;

[0021] b. Take 80% of grass green bauxite granules, 7% of 250-300 mesh clay fine powder, 6% of talcum powder, and 7% of bentonite by weight, and add 5%-8% of the above-mentioned total weight of water to fully stir , the time is about 30 minutes;

[0022] C, getting particle size by weight ratio is 80% of 15 purpose bauxite pellets (will contain AI 2 o 3 70%-80% of bauxite is crushed by a crusher and a pair of rollers, and then screened by a vibrating sieve), 7% of 250-300 mesh clay fine powder, 6% of talcum powder, and 7% of bentonite. 5%-8% water by weight is fully stirred for...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The composition of said invented environment-protecting type water-permeable brick is composed of (wt%) 75%-85% of bauxite granule material with 6-35 meshes, 7%-10% of clay fine powder with 250-300 meshes, 3%-6% of talcum powder and 4%-8% of bentonite. Said invented water-permeable brick is made up by using the above-mentioned materials in which the bauxite granule material is used as main material through the process of baking at high temperature. Said product has high strength, high hardness, strong bearing capacity and excellent water permeability, and its water-permeable rate can be up to 21mm / s.

Description

(1) Technical field [0001] The invention relates to a ground brick for laying sidewalks, in particular to an environment-friendly permeable brick. (2) Background technology [0002] The pavement hardening of urban sidewalk slabs mostly adopts the method of laying marble, glazed tiles, cement bricks to realize at present. Although the pavement paved with the above materials has the effect of being clean, beautiful and dust-proof, it also has some shortcomings: [0003] 1. Due to its extremely poor water permeability, it directly blocks the infiltration of rainwater. As a result, the urban groundwater source cannot be replenished, which aggravates the drought phenomenon in the city; [0004] 2. The reflection of sunlight on the road greatly increases the urban heat island effect; [0005] 3. It is extremely harmful to the environmental protection and plant protection of the urban area, and directly affects the growth of flowers, plants and trees. (3) Contents of the invent...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B33/00C04B33/02E01C5/00
Inventor 曹正茂曹旭东曹东辉方春红
Owner 曹正茂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products