A production method and technology for fly ash bricks, which are applied in sustainable waste treatment, solid waste management, climate sustainability, etc., can solve the problems of easy generation of shrinkage cracks, fast water absorption, high production cost, and achieve light weight, The effect of slow water absorption and low cost

Inactive Publication Date: 2007-05-02
时跃明
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, fly ash is used as the base material to produce building load-bearing blocks, and the method of building next door blocks is to use cement, ground ash, fly ash, lime, admixtures, and foaming agents as materials, and the input ratio is 2.5:1: 2∶0.2∶0.01∶0.038, the above materials are mixed according to the proportion, and then stirred. ) fast water absorption, low compressive strength, poor plastering effect, easy to produce shrinkage cracks, difficult to mechanical production, high production cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing flyash brick

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0007] A production method of fly ash bricks, comprising the steps of material selection, crushing, batching, mixing, injection of cross-linking agent, compression molding, health care treatment and the like. in:

[0008] Fly ash is selected as the base material; slag, gypsum, and lime are used as fillers; the mixture of concrete admixture and water is used as a crosslinking agent, and the weight ratio of each material in the unit weight is 55-70% for the base material and 28% for the filler. -43%, the crosslinker is 1-3%. The weight ratio of slag, gypsum and lime in the filler is: 2-3:0.1-0.4:1.0-2.0. The weight preparation ratio of concrete admixture and water in the crosslinking agent is: 0.5-1.5: 1-2. Fly ash, slag, gypsum, and lime are crushed into particles with a diameter of 100-800 microns. After preparing according to the above parameters, mix and mix evenly, inject the adhesive agent until uniform, send it to the mold for compression molding, and cure it in a kiln...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

A powdered coal ash brick with high compression strength and no shrinking and cracking is proportionally made up of powdered coal ash, slags, gypsum, lime, and the mixture of concrete additive and water through pulverizing, proportional mixing, adding said mixture as cross-linking agent, die pressing and curing.

Description

technical field [0001] The invention relates to a production method of bricks, in particular to a production method of making fly ash bricks with fly ash as the base material. Background technique [0002] At present, fly ash is used as the base material to produce building load-bearing blocks, and the method of building next door blocks is to use cement, ground ash, fly ash, lime, admixtures, and foaming agents as materials, and the input ratio is 2.5:1: 2∶0.2∶0.01∶0.038, the above materials are mixed according to the proportion, and then stirred. ) fast water absorption, low compressive strength, poor plastering effect, easy to produce shrinkage cracks, difficult to mechanical production, high production cost. Contents of the invention [0003] Aiming at the deficiencies of the prior art, the present invention provides a fly ash brick with slow water absorption speed, high compressive strength, strong bonding force with mortar, no shrinkage, no cracks, light weight, sui...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B18/08C04B28/18
CPCY02W30/91
Inventor 时跃明
Owner 时跃明
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap