Heat-insulating light sandwich wall board

A light-weight wallboard and sandwich technology, applied in building components, sustainable waste treatment, solid waste management, etc., can solve problems such as increasing processes, reducing bending and compressive resistance, and affecting the strength of wallboards, so as to increase practicality area, reduce wet work, and save the total cost

Inactive Publication Date: 2002-08-07
范广俭
View PDF0 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] After investigation, there are many domestic literatures and manufacturers on the production of wallboards with straw as raw materials. Metal plates, concrete, and wood boards are used as surface materials, and materials such as perlite, polystyrene foam, foamed resin, and honeycomb cells are sandwiched inside. , There are also manufacturers of sandwich panels, but although some of these products are also wallboards made of straw, they are hollow and have no sandwich core, and their thermal insulation performance is poor. cold and heat
However, some sandwich panels made of other materials have low strength; some are bulky and inconvenient to transport and install; some have high cost;
In short, the prior art has the following deficiencies: 1. The hollow board does not sandwich the core, and the thermal insulation and sound insulation performance is poor
2. Metal plate sandwich panel, high cost and easy to corrode
3. Concrete sandwich panels have high surface density and inconvenient construction
4. Wooden metal mesh sandwich panel, high cost, poor fire resistance
5. The sandwich wallboard cannot be formed at one time, which not only increases the process, but also affects the strength of the wallboard and reduces the bending and compressive resistance
6. The cost of some earthen wall panels is too high. General enterprises, especially the brick yards that are forced to switch production, are limited by capital and technology and are unable to take over production. Moreover, it is difficult to promote the use of wall materials that have just started

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heat-insulating light sandwich wall board
  • Heat-insulating light sandwich wall board

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0009] 1. Specific formula

[0010] Shell: straw powder 50%, light mineral powder 35%, fly ash 2.9%, halogen powder 10%, glass fiber silk 1%, gelling agent 0.5%, flame retardant 0.5%, brightener 0.05%, curing agent 0.05%,

[0011] Inner core: polystyrene foam, thickness 80mm.

[0012] 2. Manufacturing method

[0013] Match the required raw material ingredients in proportion-uniformly stir-inject into the mold-level-spread glass fiber-inject the mixed raw material for the second time-second level-place the polystyrene with a length of 2600mm×250mm×80mm Two vinyl foam boards with a 10mm gap between them-the third injection of mixed raw materials-the second time of laying glass filaments-the fourth injection-leveling (the entire operation process is completed within 20 minutes) —— Curing—— Demoulding—— Natural curing, after drying, it can be used in the factory.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The sandwich heat-insulating light wall panel is made up by using crop straw and stalk as main raw material, matching with light ore powder, gelling agent and other components and sandwiching polystyrene foam plate and utilizing special-purpose equipment through one-step process. Its composition comprises straw and stalk powder 48-50%, light ore powder 35-42%, flyash 4-8%, halide powder 10-12%, glass fibre 1-2%, gelling agent 0.2-1%, fiore-resisting agent 0.5-0.8%, whitening agent 0.05-0.1% and solidifying agent 0.01-0.09%, and its internal core is polystyrene foam plate, its thickness is 30-100 mm.

Description

1. Technical Field: [0001] The invention belongs to a new type of building material, and specifically relates to a kind of integrated sandwich insulation made of crop straw as the main raw material, with light mineral powder, gelling agent, polystyrene foam material inside, and special equipment at one time. Insulated lightweight wall panels. 2. Background technology: [0002] After investigation, there are many domestic documents and manufacturers about the production of wallboard using straw as raw materials. Metal plates, concrete, and wood panels are used as surface materials, with perlite, polystyrene foam, foamed resin, honeycomb-shaped cells and other materials. , There are manufacturers of sandwich panels, but some of these products are also wall panels produced from straw, but they are hollow and not sandwiched, and have poor thermal insulation performance. They are not ideal for external walls and roof panels, and are difficult to resist the north. Cold and hot. Some sa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B30/00
CPCC04B30/00C04B2111/00612Y02W30/91C04B14/36C04B14/42C04B18/08C04B18/24C04B22/12C04B2103/0068C04B2103/445
Inventor 范广俭
Owner 范广俭
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products