Water-resistant corrosion-resistant paint or water-resistant factice produced by using industrial organic waste as raw material

A technology of organic waste and anti-corrosion coatings, applied in the direction of anti-corrosion coatings, rosin coatings, epoxy resin coatings, etc., to achieve the effects of reducing pollution, obviously comprehensive social and economic benefits, and reducing costs

Inactive Publication Date: 2003-08-06
JIANGNAN UNIV
View PDF0 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are no reports of relevant comprehensive treatment methods at home and abroad

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] A water-resistant and anti-corrosion coating is prepared from 20.0% of organic waste, 30.0% of epoxy resin, 2.0% of SBS glue, 25% of filler, 1% of auxiliary agent and 22.0% of mixed solvent.

Embodiment 2

[0046] A water-resistant and anti-corrosion coating is prepared from 28% of phenolic resin, 26.0% of organic waste, 2.0% of SBS glue, 15% of filler, 28.0% of mixed solvent and 1% of auxiliary agent.

Embodiment 3

[0048] A water-resistant and anti-corrosion coating is prepared from 30.0% of polyurethane resin, 25.0% of organic waste, 3.0% of SBS glue, 12.0% of filler, 29.0% of mixed solvent and 1% of auxiliary agent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to a water-proofing anticorrosion coating material or building oil-containing semi-solid composition produced by using industrial organic wastes and its preparation method. The water-proofing anticorrosion coating material is a monocomponent or double-component resin modified imitation asphalt paint made up by compounding industrial organic wastes, modifying resin, SBS sizing material, mixing solvent, adjuvant, filler and solidifying agent, and the building oil-containing semi-solid composition is made up by mainly using industrial organic wastes, polyvinyl chloride resin and SBS sizing material as modifying agent. Said products are water-proof, and have strong anticorrosion performance, and their production process is simple.

Description

technical field [0001] A water-resistant and anti-corrosion coating or a building waterproof ointment produced by using industrial organic waste as a raw material and a preparation method thereof. The invention relates to the technical field of comprehensive treatment of semi-solid colloidal organic waste. Background technique [0002] Environmental pollution is one of the problems faced by my country's economic development and social progress. Environmental pollution not only destroys the ecological balance, wastes resources and energy, but also seriously endangers human health and survival, and also hinders the further development of industrial and agricultural production. At present, China pays more attention to the treatment of waste gas, waste water, and urban garbage pollution, but not enough attention is paid to industrial solid waste. Improper treatment will cause secondary pollution and endanger the environment. This should arouse the attention of relevant departme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D5/08C09D125/16C09D161/06C09D163/00C09D175/04C09D193/04
Inventor 刘晓亚陈明清奚冬雷熊万斌杨成倪忠斌
Owner JIANGNAN UNIV