Semiconductive ceramic thick film heating material

A technology of heating materials and semiconducting ceramics, applied in the direction of heat exchange materials, chemical instruments and methods, etc., can solve the problems of unstable performance, fast power attenuation, large square resistance of materials, etc., and achieve small square resistance and high temperature stability Good, good resistance to cold and heat shock

Inactive Publication Date: 2004-04-21
厦门康美达科技有限公司
View PDF0 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the above-mentioned materials have low heating temperature, some (such as PTC ceramic chips) have lead pollution, and cannot work under no-load conditions, which limits their application.
The oxide thick-film heating materials developed in modern times also have unstable performance. When the surface temperature exceeds 600°C, the power decays quickly and the material square resistance is large.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

2

1

[0026] Sintering temperature: 1200-1350 degrees Celsius;

[0027] The substrate material is: alumina porcelain or chemical porcelain, and the substrate shape can be flat or tubular;

[0028] Its square resistance ranges from 2 ohms / square (Ω / □) to 500 kiloohms / square (KΩ / □). According to needs, after applying the rated working voltage, the heating temperature ranges from tens to 800 degrees Celsius.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
ignition pointaaaaaaaaaa
Login to view more

Abstract

A semi-conducting thick ceramic film as heat generating material is prepared through proportional mixing function phase with adhesive phase, adding organic carrier to prepare slurry, preparing electrothermal heat-generating material, coating it on substrate and high-temp sintering. Said function phase is composed of one of Ge, Si and C or more single elements and multiple oxides, which play the role of characteristic modifiers.

Description

technical field [0001] The invention belongs to the technical field of thick film electronic materials and electric heating. technical background [0002] Thick-film electronic materials and technologies in the prior art have been widely used, mainly in thick-film integrated circuit technology and electronic chip component technology. These thick film materials are mainly used as conductors and resistive and capacitive components for information processing, and have no electric heating function. Electric heating technology has a long history. For a long time, most of the heating elements used in household appliances and fields such as industry, agriculture, medicine, and scientific research are electric heating wires or electric heating tubes. Traditional resistance wires have low heating efficiency and short life, and cannot operate at low voltage ( Such as working under 12V) and other shortcomings. The heating elements developed in the 1970s to replace electric heating t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09K5/14
Inventor 王培英白铁城
Owner 厦门康美达科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products