Powder metallurgy internal hilical gear, and its manufacturing method and die using same method

A technology of internal helical gear and powder metallurgy, which is applied in the field of powder metallurgy internal helical gear and its manufacturing and implementation of the mold, can solve the problems of increasing raw material loss, difficulty in withdrawing the mandrel, and high manufacturing cost, so as to save raw materials and manufacture The effect of low cost and compact mold structure

Inactive Publication Date: 2004-09-15
JIANGSU YINGQIU GRP CO LTD
View PDF0 Cites 22 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This kind of internal helical gear cannot be processed in China by stamping and rolling.
When the internal helical gear is pressed by the general powder metallurgy method, the mandrel is difficult to withdraw, especially if the helix angle is large, the compact will be damaged
Even if the processed internal helical gea

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Powder metallurgy internal hilical gear, and its manufacturing method and die using same method
  • Powder metallurgy internal hilical gear, and its manufacturing method and die using same method
  • Powder metallurgy internal hilical gear, and its manufacturing method and die using same method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] Attached below Figure 1-2 Embodiments of the present invention will be further described in detail.

[0018] The sintering treatment is not to completely melt the material powder into an alloy. The sintering treatment is to heat-treat the formed body of the metal or alloy powder under pressure at a temperature below the melting point of the main element, and use the solid solution phenomenon produced by the combination of powders to sinter. into.

[0019] The technical scheme of the powder metallurgy internal helical gear of the present invention is that, by weight percentage, the composition of the above-mentioned internal helical gear contains alloy elements Cu 1-3%, Ni 1-3%, Mo 0.1-1%, and the rest is Fe and unavoidable ingredients.

[0020] figure 1 As shown, in the batching and mixing process A, the raw material powder composed according to the proportion of pre-alloyed steel powder containing Cu 1-3%, Ni 1-3%, Mo 0.1-1%, and the rest is Fe The mixture is a bi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a powder metallurgical internal inclined gear, according to weight percent, containing elements Cu 1-3%, Ni 1-3%, Mo 0.1-1%, and the rest Fe and unavoidable component, where its spiral angle is not greater than 35 degrees, its pressure angle is 5-25 degrees, and its mode is 0.5-2.5 degrees. It mixes the alloy powder of Cu, Ni and Mo to make press molding, firing and shaping so as to make it. Its making mould is top, bottom and middle moulds and core stick. It gears stably and accurately, has small friction coefficient and low mechanical noise. It adopts special designed mould, presses by mould core's rotary ascending or descending along screw, which converts the rotary pressing into axial pressing, can press internal inclined gears of various spiral angles.

Description

technical field [0001] The present invention relates to a kind of special-shaped product manufactured by metal powder and its manufacturing method and equipment, in particular, it relates to a powder metallurgy manufacturing internal helical gear, its manufacturing method and special equipment. technical background [0002] At present, gear transmission is widely used in various machines, automobiles, clocks, instruments, electrical appliances and other industries. It has stable transmission ratio, accurate and reliable transmission motion, high transmission efficiency, especially internal helical gear transmission, its advantages are more obvious, except In addition to the characteristics of general gear transmission, it also has the characteristics of compact structure. This internal helical gear adopts stamping and rolling domestic still can't process. When the internal helical gear is pressed by the general powder metallurgy method, the mandrel is difficult to withdraw,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22F5/08C22C38/16
Inventor 陈秀发
Owner JIANGSU YINGQIU GRP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap