Antifogging coating composition and article coated therewith

一种防雾涂料、组合物的技术，应用在涂层、对表面涂布液体的装置等方向，能够解决很难擦掉污染、污染、流水的痕迹显著等问题

Inactive Publication Date: 2004-10-06
NOF CORP
View PDF0 Cites 18 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at the same time, a water film is formed on the surface of the anti-fog coating film after hardening, and the water is flowed down to be dried, but there is a problem in appearance that traces of running water are conspicuous and cause contamination
[0005] In the case when an anti-fog coating film is formed on the inner surface such as a meter cover or a lamp cover, it is difficult to wipe off the contamination of running water traces due to the structure of the meter or lamp

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0094] Hereinafter, the present invention will be further explained by referring to Reference Examples, Preparation Examples, Examples and Comparative Examples. Hereinafter, % means % by weight.

[0095] Reference example 1 (preparation of block polymer A)

[0096] In a reactor equipped with a thermometer and a stirrer, 550 g of propylene glycol monoethyl ether was added as an organic solvent. The reactor was simultaneously heated to 70° C. under the nitrogen gas flow. In the reactor, drop the mixed solution in 2 hours, and its component is 5g polyperoxide as the initiator of polymerization reaction, and its molecular formula is as shown in (6); 135g of N,N-dimethylacrylamide as a water-soluble vinyl monomer; and 15 g of N-methylolacrylamide as a crosslinkable vinyl monomer. Then, a polymerization reaction was carried out for another 2 hours, thereby synthesizing a matrix of a block copolymer.

[0097] Then, within 1 hour, a mixed solution consisting of 140 g of methyl met...

example 1

[0111] Example 1 (preparation of anti-fog coating composition)

[0112] Anti-fog coating composition is mixed by following compound: 140g block copolymer A (solution) prepared by reference example 1, 2g sodium dioctylsulfosuccinate (produced by NOF company, product name: RapizolA-80) , 0.5g polyoxyethylene octyl phenyl ether (produced by NOF company, product name: Nonion discloses HS-210HS-210), diisobutyl phosphate as surfactant, and organic silicon additive (Toray organic Silicon company production, product name: SH28PA).

[0113] The composition ratio (parts by weight, block copolymer / surfactant / acid alkyl phosphate) in the solid component of the anti-fog coating composition is 100 / 5 / 0.1.

example 2-5 and comparative example 1-4

[0114] Example 2-5 and comparative example 1-4 (preparation of anti-fog coating composition)

[0115] The anti-fog coating compositions in Examples 2-5 and Comparative Examples 1-4 were prepared according to the method shown in Example 1, but the types and amounts of materials used were changed. The types and amounts of materials used in the anti-fog coating composition and the final results of preparation are shown in Table 1 and Table 2.

[0116] example

1

2

3

4

5

Block copolymer A (g)

140

140

0

0

140

Block copolymer B(g)

0

0

0

140

0

Graft copolymer (g)

0

0

165

0

0

Random Copolymer (g)

0

0

0

0

Surfactant

(g)

a

2

4

5.4

2

0

b

0.5

1

1.5

0.5

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
boiling pointaaaaaaaaaa
conversion efficiencyaaaaaaaaaa
Login to View More

Abstract

An antifogging paint composition for forming an antifogging coating film without generation of the running water trace. The antifogging paint composition contains a block or grafted copolymer comprising a hydrophilic polymer part formed from a vinyl monomer having a cross-linking functional group and a water-soluble vinyl monomer, and a hydrophobic polymer part formed from a non water-soluble vinyl monomer, and an acidic alkyl phosphate.

Description

technical field [0001] The invention relates to an anti-fog coating composition. More specifically, the present invention relates to an antifog coating composition for forming an antifog coating film on the surface of a transparent plastic material or glass material, and a coating substance having the formed coating film. Background technique [0002] Conventional thermosetting antifog compositions using random copolymers do not have sufficient adhesion properties to plastic or glass substrates. The present inventors disclosed a thermosetting antifogging agent composition having enhanced adhesion properties in Japanese Laid-Open Patent Publication Nos. hei6-212146 and hei6-107967. In the case of forming a coating film with an antifogging agent composition, in order to obtain a hard coating film with good properties, severe process conditions are required: a high temperature of 120° C. or higher and a hardening time of 30 minutes or longer. Sin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F265/04C08F283/06C08F291/00C08F293/00C08F297/00C08K5/521C09D133/06C09D151/00C09D153/00
CPCC08F291/00C08K5/521C08F297/00C09D151/003C08F265/04C09D133/066C08F293/005C08F283/06C09D153/00C09D151/00C08L53/00C08L2666/02C08L2666/40C09D133/06
Inventor 滝塚典和原田英治杉浦正人
Owner NOF CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com