Water paint for protecting surface of car and household electrical apparats

A technology for protecting coatings and automobiles, applied to devices and coatings that apply liquid to the surface, and can solve problems such as peeling, aging, and discoloration

Inactive Publication Date: 2005-01-05
徐厚训
View PDF0 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Nowadays, automobiles and home appliances, especially automobiles, often have the following problems during storage and transportation: in the open parking lot, due to the erosion of rain, especially acid rain, humidity and sunlight, the paint coating will be damaged. Phenomena such as light, discoloration, cracks, peeling, peeling and aging
So far there is no other better way to effectively protect the surface of automobiles and home appliances

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Water paint for protecting surface of car and household electrical apparats

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A water-based protective coating for the surface of automobiles and home appliances, a water-based resin emulsion composed of 85 parts of acrylic resin, 25 parts of styrene acrylic modified resin, and 10 parts of epoxy resin, 3.5 parts of a reinforcing agent, 3 parts of a thixotropic agent, and a film-forming agent 4 parts, wherein: the reinforcing agent is silicon dioxide with a particle diameter of 15um, the thixotropic agent is carboxymethylcellulose with a molecular weight of 1500, and the film-forming agent is propylene glycol.

Embodiment 2

[0018] A water-based protective coating for the surface of automobiles and home appliances, a water-based resin emulsion composed of 70 parts of acrylic resin, 10 parts of styrene acrylic modified resin, and 5 parts of epoxy resin, 1 part of reinforcing agent, 1 part of thixotropic agent, and film-forming agent 1 part, wherein: the reinforcing agent is silicon dioxide with a particle diameter of 12um, the thixotropic agent is methylcellulose with a molecular weight of 1900, and the film-forming agent is ethylene glycol. 0.1 part of silicone defoamer was also added.

Embodiment 3

[0020] A water-based protective coating for the surface of automobiles and home appliances, a water-based resin emulsion composed of 78 parts of acrylic resin, 15 parts of styrene acrylic modified resin or other modified acrylic resin, 8 parts of epoxy resin, 2 parts of reinforcing agent, and thixotropic agent 2 parts, 3 parts of film-forming agent, wherein: the reinforcing agent is silicon dioxide with a particle diameter of 10um, the thixotropic agent is hydroxyethyl cellulose with a molecular weight of 6000, and the specific composition of the film-forming agent is 1 part of ethylene glycol, propylene glycol 2 servings. Also added 1.5 parts of silicone defoamer.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
peel strengthaaaaaaaaaa
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a water protective paint for automobile and domestic surfaces, and its weight proportions: a water resin latex composed of acrylic resin 70-85 shares, modified acrylic resin 10-25 shares and epoxy resin 5-10 shares, reinforcing agent 1-3.5 shares, thixotropic agent 1-3 shares and film-forming agent 1-4 shares; where the reinforcing agent is silicon dioxide with particle size below 15 mum, the thixotropic agent is fibrin compound with molecular weight 1500-6000, and the film forming agent is one or two of the glycol and propylene alcohol. It has proper strength, hardness, flexibility and elongation. It has no bad effect on original paint coated surfaces of automobiles, home appliances, etc and can play a good role in protecting.

Description

Technical field: [0001] The invention relates to the field of paint industry, in particular to a water-based protective paint for the surface of automobiles and home appliances. Background technique: [0002] Nowadays, automobiles and home appliances, especially automobiles, often have the following problems during storage and transportation: in the open parking lot, due to the erosion of rain, especially acid rain, humidity and sunlight, the paint coating will be damaged. Light, discoloration, cracks, peeling, peeling and aging. Dust, dust, oil stains, fingerprints and other dirt during storage and transportation will seriously pollute the surface coating of the car, and even be stained with variegated colors, which will make the whole car look old and affect the appearance and sales. Scratches and abrasions during storage and transportation will reduce the surface quality, and serious cases will cause repairs and increase costs. For this reason, in order to prevent the o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B05D7/14C09D133/00
Inventor 徐厚训
Owner 徐厚训
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com