Anticorrosive treated material for highway rail boards and building wall boards and process thereof

A technology for highway guardrail and anti-corrosion treatment, applied in the field of anti-corrosion of building wall panels and highway guardrail panels, can solve the problems of short service life, human injury, environmental pollution, etc., and achieve the effect of long service life

Inactive Publication Date: 2005-02-23
TAOYUAN NANOMETER INST HANDAN CITY
View PDF0 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention is intended to solve the problems in the prior art of pollution to the environment, harm to the human body, hardw

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0005] The material used in the present invention is composed of bottom glaze and surface glaze, wherein the bottom glaze is composed of bottom glaze itself and nanocomposite material, and the weight percentages of bottom glaze are respectively: SiO 2 50%, TiO 2 3.4%, Al 2 o 3 3.8%, CaO 2.8%, Na 2 O 13%, K 2 O 2.6%, Li 2 O 3.6%, B 2 o 3 13.2%, CoO 0.8%, NiO 3%, CuO 0.8%, MnO 3%, the composition and weight percentage of nanocomposite materials are: Al 2 o 3 70%, ZrO 3 1%, SnO 2 18%, TiO 2 11%; the composition and weight percentage of the top glaze are: SiO 2 45%, Al 2 o 3 2%, CaO 2%, Na 2 O 12%, K 2 O 2.5%, Li 2 O 4%, ZnO 4%, B 2 o 3 15.5%, Na 2 SiF 6 4% and TiO 2 9% composition. The production process adopted to solve the problems existing in the prior art is: (1) SiO in the bottom glaze and the top glaze 2 and Al 2 o 3 Purify at high temperature; (2) Grind and sieve the bottom glaze and surface glaze materials to 80 mesh respectively, whe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A new antiseptics and process for highway safety guards and construction walling board, belonging to a new antiseptic material and process for hardware, especially referring to antisepsis of highway safety guards and construction walling board. Using inorganic material to be primary coat and surface coat, having resolved the pollution problem of technology currently, decreasing the injury of worker, prolonging using life. The main material of primary coat are SiO2, TiO2, Al2O3, CaO and so on and the main material of surface coat are SiO2, Al2O3, CaO, Na2O and so on. The materials are painted to the surface of hardware by grinding, riddling and nodulizing.

Description

(1) Technical field: [0001] The invention belongs to a new anticorrosion treatment material and technology for hardware, and in particular relates to the anticorrosion of road guardrail boards and building wall boards. (two) background technology: [0002] The anti-corrosion treatment of hardware generally adopts pickling, hot-dip galvanizing, aluminum plating, plastic spraying, and spray painting procedures. Because the pickling process needs to use a large amount of acid to treat the rust on the metal surface, in addition to the damage to the metal surface In addition to corrosion, it also poses a direct threat to the health of the staff, and work accidents often occur. At the same time, the corrosion of the acid on the plant, the surrounding flowers and trees, and the ecology of the area where the acid liquid flows through will cause direct damage and impact. No matter the production process Or use the process will produce absolute pollution to the environment. Anti-corr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C8/02C03C8/22C04B41/52C23D5/00C23D11/00
CPCC03C3/118C03C8/02C03C3/093C03C8/22
Inventor 吕山岭奚惠先柳河昌刘玉凯朱斌
Owner TAOYUAN NANOMETER INST HANDAN CITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap