Cement based environmental Protection mortar powder and preparation method

A cement-based, mortar powder technology, applied in the direction of sustainable waste treatment, solid waste management, climate sustainability, etc., can solve problems such as difficult to accurately grasp the amount of auxiliary materials added, difficult to ensure project quality, and affect the quality of mortar, etc. Achieve the effects of overcoming cracks, turning waste into treasure energy, and mixing more sand

Inactive Publication Date: 2005-03-30
GUANGXI YINGYI ENVIRONMENTAL PROTECTION BUILDING MATERIALS TECH CO LTD
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The traditional cement-based mortar preparation is generally made by mixing cement, sand and water manually or with a mortar mixer. The general sand ratio is 1 to 3, that is, 1 kg of cement is mixed with 3 kg of sand; Other auxiliary materials must be added, such as lime powder, finely ground fly ash, lime paste, mortar admixture, etc. to solve the consistency problem of the mortar, which is not only troublesome to use, but also difficult to accurately grasp the amount of auxiliary materials added. It affects the quality of the mortar, makes it difficult to guarantee the quality of the project, and directly affects the quality of the building.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Prepare 325# cement-based environmental protection mortar powder ingredients ratio of each component (Kg):

[0025] >50Mpa cement clinker 45

[0026] Fly Ash 30

[0027] lime slag 8

[0028] Waste bricks and tiles 10

[0029] plaster 4

[0030] Mortar Thickener 3

[0031] (Mortar thickening powder is the product of Chinese patent number ZL 00131519.6)

[0032] The above-mentioned raw materials are pulverized, mixed, and sieved with a 0.08mm square hole sieve, so that the sieve residue is less than 10% to obtain the finished product.

[0033] Mortar label

Embodiment 2

[0035] Prepare 325# cement-based environmental protection mortar powder ingredients ratio of each component (Kg):

[0036] 42.5 ordinary cement 50

[0037] Fly Ash 30

[0038] Waste bricks and tiles 8

[0039] lime slag 5

[0040] plaster 4

[0041] Mortar thickening powder (kind is the same as embodiment 1) 3

[0042] Manufacturing process is the same as embodiment 1. The properties of M10.0 and M7.5 mortars prepared with the cement-based environmentally friendly mortar powder produced by the above ingredients are also the same as in Example 1.

Embodiment 3

[0044] Prepare 275# cement-based environmental protection mortar powder ingredients ratio of each component (Kg):

[0045] >50Mpa cement clinker 35

[0046] Fly Ash 35

[0047] Slag 10

[0048] Waste bricks and tiles 10

[0049] plaster 5

[0050] lime slag 3

[0051] Mortar thickening powder (kind is the same as embodiment 1) 2

[0052] Mortar

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A cement base environmental protecting motar powder, the components in mass portion are: common portland cement or cement semi-finished product 10-50, industrial waste residue 30-80, plaster 2-8, motar thickening agent 1-3. The prodn. method is to mix said materials weighted according to grade matching composition of design, then to levigate them to obtain product, the fineness is controlled in 0.08mm, the sieved margin of square hole screen is less than 10 percent.

Description

technical field [0001] The invention belongs to the field of cement-based mortar powder and a preparation method thereof. Background technique [0002] The traditional cement-based mortar preparation is generally made by mixing cement, sand and water manually or with a mortar mixer. The general sand ratio is 1 to 3, that is, 1 kg of cement is mixed with 3 kg of sand; Other auxiliary materials must be added, such as lime powder, finely ground fly ash, lime paste, mortar admixture, etc. to solve the consistency problem of the mortar, which is not only troublesome to use, but also difficult to accurately grasp the amount of auxiliary materials added. It affects the quality of the mortar, makes it difficult to guarantee the quality of the project, and directly affects the quality of the building. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a cement-based environme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B18/04C04B22/14C04B28/04
CPCY02W30/91
Inventor 陈益兰谢盈庭
Owner GUANGXI YINGYI ENVIRONMENTAL PROTECTION BUILDING MATERIALS TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products