Method for preparing tungsten base high specific gravity alloy board
A high specific gravity, alloy plate technology, applied in metal rolling, metal rolling, metal processing equipment and other directions, can solve the problems of high production cost, easy cracking, high cost, achieve excellent mechanical properties, improve thermoplasticity, production process less effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
preparation example Construction
[0014] A preparation method of a tungsten-based high specific gravity alloy plate is characterized in that the preparation process is as follows: a. W powder with Fsss Fisherman's average particle size of 2.8 to 3.2 μm, nickel Ni powder, iron Fe powder, and a small amount of cobalt Co powder and yttrium Y powder are mixed and compacted in a mixing machine; b. Under the protection of hydrogen gas, the billet is heated to 1490°C-1500°C in a sintering furnace at a rate of 15°C / min for 2 hours to obtain a slab; c. .Using the stainless steel plate as the jacket material for the prepared slab to carry out jacket rolling, the rolling temperature is 700 ℃ ~ 900 ℃, the processing rate of the first pass is 25% ~ 30% when the billet is opened, and then every The pass processing rate is 18% to 23%, and when the total processing rate reaches 45% to 50%, the vacuum degree is 6×10 -3 Pa, the temperature is 1000 ℃ ~ 1250 ℃, vacuum heat treatment for 1 ~ 2 hours to eliminate stress; then choos...
Embodiment 1
[0018] Put tungsten W powder with Fsss average particle size of 2.8-3.2 μm, nickel Ni powder, iron Fe powder, trace amount of cobalt Co powder and yttrium Y powder in a mixer with a steel ball to raw material weight ratio of 5:2 , the mixing time is 12 hours, the rotating speed of the drum is 40r / min, and it stops for 20min at 6 hours. Press the billet, under the protection of hydrogen gas, heat the billet in the sintering furnace at a rate of 15°C / min to 1490°C for 2 hours to obtain a slab; use the prepared slab thickness of 1.2mm stainless steel plate as the sheathing material, carry out Sheath rolling, the rolling temperature is 700°C, the processing rate of the first pass is 25% when the billet is opened, and the processing rate of each subsequent pass is 18%. When the total processing rate reaches 45%, alkali washing and alkali cleaning The liquid ratio is 85% NaOH + 15% KNO 3 , Alkali temperature: 380 ℃, alkaline washing for 10 minutes, after the alkaline washing time i...
Embodiment 2
[0020] Mix tungsten W powder with Fsss average particle size of 2.8-3.2 μm, nickel Ni powder, iron Fe powder, trace amount of cobalt Co powder and yttrium Y powder in a mixer with a steel ball to raw material weight ratio of 5:1 Inside, the mixing time is 12 hours, the rotating speed of the drum is 60r / min, and it stops for 20min at 6 hours. Press the billet, under the protection of hydrogen gas, heat the billet in the sintering furnace at a rate of 15°C / min to 1500°C for 2 hours to obtain a slab; c. Use the prepared slab thickness of 1.7mm stainless steel plate as the sheathing material , carrying out clad rolling, the rolling temperature is 900°C, the processing rate of the first pass is 30% when the billet is opened, and the processing rate of each subsequent pass is 23%, and when the total processing rate reaches 50%, alkali cleaning is carried out. The ratio of lye is 85%NaOH+15%KNO 3 , Alkali temperature: 500 ℃, alkaline washing time: 2 minutes, after alkaline washing, ...
PUM
Property | Measurement | Unit |
---|---|---|
Granularity | aaaaa | aaaaa |
Thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap