Covering agent for pouring basket in high alkalinity

A tundish and covering agent technology, which is applied in the field of auxiliary materials for continuous casting of steel making, can solve the problems such as the production of steel grades that are not suitable for S requirements, the carbonization of molten steel is easy to increase, and the capacity is not ideal, so as to improve the quality of the casting billet, Good thermal insulation performance and the effect of preventing secondary oxidation

Inactive Publication Date: 2005-08-31
BAOSHAN IRON & STEEL CO LTD
View PDF2 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0009] Disadvantages: for protection and absorption of Al 2 o 3 The capacity is not ideal, the molten steel is easy to carburize or absorb hydrogen
[0012] Disadvantages: Poor insulation effect
[0015] Disadvantages: It is less effective to isolate the air and prevent the secondary oxidation of molten steel
For example, U.S. Patents US6174347B1 and US6179895B1 are high-basic tundish covering agents, but they use the slag refined by the Ladle Metallgy Furnace as the main raw material, and the content of impurity elements such as S in this material Relatively high, not suitable for the production of steel grades that require S

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Covering agent for pouring basket in high alkalinity
  • Covering agent for pouring basket in high alkalinity
  • Covering agent for pouring basket in high alkalinity

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0042] See Table 2 for examples and comparative examples of the high alkalinity tundish covering agent of the present invention.

[0043]

Example

Composition (mass percentage)

Alkalinity

Effect

calcium aluminate

calcium carbonate

Magnesia

Quartz sand

binder

Admixture

lining erosion

1

87.1

3.9

0.1

1.9

6.0

1.0

8.51

Nothing serious

2

89.9

0.3

2.2

4.5

1.7

1.4

6.00

Nothing serious

3

71.2

24.1

0.8

3.0

0.1

0.8

10.71

Nothing serious

4

72.3

3.6

14.2

0.7

9.1

0.1

12.10

Nothing serious

5

73.5

21.3

2.8

0.9

0.3

1.2

11.18

Nothing serious

6

75.5

7.2

11.0

1.1

3.0

2.2

16.48

Nothing serious

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

A high-basicity covering agent for the tundish to decrease O2 and S from molten steel, and prevent secondary oxidizing is proportionally prepared from the calcium aluminate prepared from calcium carbonate and bauxite, magnesium sand, adhesive chosen from dextrin, wheat flour and water glass, additive chosen from phosphate, lignosulfonate, citric acid glycerine, etc, calcium carbonate and quartz sand.

Description

technical field [0001] The invention relates to an auxiliary material for continuous casting in steelmaking, in particular to a tundish covering agent. Background technique [0002] The tundish for storing and transporting molten steel is a transitional reactor in the metallurgical process. It is used to distribute the molten steel transported by the ladle to the mold, stabilize the pouring speed, reduce the impact momentum of the injection flow in the mold, and remove steel. Ideal place for inclusions in the water. [0003] The tundish covering agent is a granular or powder artificial synthetic auxiliary material added on the molten steel surface of the tundish. Isolate air to prevent secondary oxidation of molten steel; (3) Absorb non-metallic inclusions floating on the surface of molten steel. [0004] At present, the commonly used tundish covering agents are divided into three categories: acid slag, neutral slag and alkaline slag. The specific types and components are ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More