Foaming concrete lightweight wall material in situ production method

A light-weight wall and the technology of the production method are applied in the preparation of building wall materials and the production of on-site foamed concrete light-weight wall materials, which can solve the problems of large materials, inconvenient on-site construction, and large floor space. Achieve the effect of easy to obtain raw materials, simple construction and low cost

Inactive Publication Date: 2006-05-10
SHENYANG JIANZHU UNIVERSITY
View PDF4 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the wall material given in the above technical proposal can be poured directly on site, too many materials are added and the floor area is too large, which brings inconvenience to the site construction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] Mix 7% hydrogen peroxide with water evenly, and mix 5% aluminum powder with cement, sand, and stone evenly. The mixing ratio of cement, sand, and stone is 1:2:3, and then mix the two mixtures quickly. Mixing, stirring and pouring into the built template, after 4 hours (20°C), the concrete can be foamed in the template and finally formed with a density of 1800kg / m 3 of the wall.

Embodiment 2

[0018] Mix 5% hydrogen peroxide with water evenly, and mix 3.5% aluminum powder with cement, sand, and stone evenly. The mixing ratio of cement, sand, and stone is 1:2:3, and then mix the two mixtures quickly. Mixing, stirring and pouring into the built template, after 4 hours (20°C), the concrete can be foamed in the template and finally formed with a density of 1900kg / m 3 of the wall.

Embodiment 3

[0020] Mix 3% hydrogen peroxide with water evenly, and mix 2% aluminum powder with cement, sand, and stone evenly. The mixing ratio of cement, sand, and stone is 1:2:3, and then mix the two mixtures quickly. Mixing, stirring and pouring into the built template, after 4 hours (20°C), the concrete can be foamed in the template and finally formed with a density of 2100kg / m 3 of the wall.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparing method of on-site foaming concrete lightweight wall material in the architecture wall material preparing technique domain, which comprises the following steps: mixing the hydroperoxide of 5-10 percent water weight and water evenly; blending the aluminum powder of 2-7 percent cement, cement, sand and stone uniformly; pouring two mixtures in the built mould; foaming the concrete in the mould to form strength after 4 hours at 20 deg.c; demoulding to obtain the wall of 1900kg / m3 density.

Description

technical field [0001] The invention relates to a method for manufacturing a foamed concrete lightweight wall, in particular to a method for manufacturing an on-site foamed concrete lightweight wall material, which belongs to the preparation technology of building wall materials. Background technique [0002] The basic requirement of building wall materials is to have a certain strength and good thermal insulation and sound insulation effects. At present, building wall materials generally adopt sintered bricks, hollow bricks, foam blocks or other composite lightweight wall materials. Plastic (polystyrene) waste, 5-15 parts by weight of ceramic powder with a particle size not greater than 1mm, 20-40 parts by weight of fly ash and 100 parts by weight of cement are mixed evenly, and an appropriate amount of water is added to make a paste. "A Foamed Plastic Ceramic Fly Ash Cement Lightweight Wall Material" that is solidified in a mold that requires specifications; Chinese inven...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04B2/84
Inventor 王博
Owner SHENYANG JIANZHU UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com