High temperature resistant and high pressure resistant ethylene propylene terpolymer synthetic rubber and preparation process thereof
A technology of EPDM and synthetic rubber, which is applied in the field of rubber or its derivatives, can solve the problems of low cost and limited application range, and achieve the effects of prolonging service life, wide application range and reasonable compatibility
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0027] Example 1
[0028] Take 24 parts by weight of EPDM 4045 rubber to be mixed with the front roller temperature of 50-60℃ and the back roller temperature of 60-70℃, add it into the open type rubber mixer and repeat the mastication 28 times, the first 4 Adjust the roller distance to 5mm in the next 5 minutes, and adjust the roller distance to 2mm in the next 5 minutes, relax the back roller under the sheet, and hit three triangle bags to make the sheet material into a strip shape that is beneficial to the subsequent process; take 10 parts by weight of high wear-resistant carbon black After mixing with 5 parts by weight of spray carbon black evenly, it becomes mixed carbon black for standby; add 1 / 2 part by weight of mixed carbon black, 1 part by weight of tertiary oil, 1 part by weight of antioxidant MB, and 0.3 parts by weight of antioxidant. 124 rolling for 5 minutes; then add 1 part by weight of active zinc oxide, the remaining mixed carbon black, 1 part by weight of ferrous...
Example Embodiment
[0029] Example 2
[0030] When the temperature of the front roller of the rubber mixer reaches 55℃ and the temperature of the rear roller reaches 65℃, add 20 parts by weight of EPDM 4045 rubber into the open rubber mixer for repeated mastication 30 times. The roller distance is 5mm in the first 5 minutes. After 6 minutes, the roll distance is 2mm. After relaxing, roll down the sheet and hit three triangle bags to make the sheet material into strips to facilitate the subsequent process; take 12 parts by weight of high wear-resistant carbon black and 4 parts by weight of spray carbon black, After the two are evenly mixed, they become mixed carbon black for use; in turn, add 1 / 2 of the mixed carbon black, 3 parts by weight of the third line oil, 0.3 parts by weight of antioxidant MB, 1 part by weight of antioxidant 124 and roll for 8 minutes; Add 2 parts by weight of activated zinc oxide, the remaining mixed carbon black, and 2 parts by weight of the ferrous metal peroxide DCP produc...
Example Embodiment
[0031] Example 3
[0032] Under exactly the same conditions as in Example 2, take 23 parts by weight of EPDM 4045 rubber into the rubber mixing machine for mastication; take 11 parts by weight of high wear-resistant carbon black and 4.5 parts by weight of spray carbon black, and mix the two After being uniform, it becomes a mixed carbon black for later use; sequentially add 1 / 2 of the mixed carbon black, 2 parts by weight of the third line oil, 0.8 parts by weight of antioxidant MB, 0.5 parts by weight of antioxidant 124, and roll for 8 minutes; then add 1.5 parts in turn The zinc oxide, the remaining mixed carbon black, and 1.5 parts of DCP continue to be mixed and released to form the finished product.
[0033] Serial number
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap