Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Multi-effect putty lacquer and its making technology

A technology of putty and water repellent, applied in the direction of filling slurry, etc., can solve the problems of water resistance, complicated construction, easy powder removal, etc., and achieves the effect of simple environmental requirements, convenient construction operation and saving construction time.

Inactive Publication Date: 2006-10-11
王明喜
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The materials used to decorate the wall are imitation porcelain paint and latex paint. The general imitation porcelain paint is not water-resistant, has poor hardness, is easy to powder, and is easy to age. The better imitation porcelain tempered paint in the imitation porcelain paint has high hardness Yes, but the washing resistance is poor and the color is single. In addition, the imitation porcelain coating has relatively high requirements in the construction process. The construction methods of polyurethane imitation porcelain coating, silicone acrylic resin imitation porcelain coating and water-soluble polyvinyl alcohol imitation porcelain coating are not the same. , need to be strictly distinguished, and no matter what kind of coating construction method, the construction requirements environment and difficulty are relatively large; while the water scrub resistance of latex paint is poor, and the hand feel is poor. The construction process of latex paint is that the wall needs to be scraped Scrape the putty two to three times on the board, then sand it with sandpaper, and then paint the latex paint on the smooth wall. The process is more complicated and takes more time. In addition, the cost of high-grade latex paint is relatively high, and quite expensive
Therefore, whether it is imitation porcelain paint or latex paint, there are problems that the effect is not ideal and the construction is complicated.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment approach 1

[0013] Take 500 parts of Shuangfei powder; 110 parts of ash calcium powder; 4.1 parts of hydroxypropyl methylcellulose; 160 parts of water; 55 parts of nano water repellent;

[0014] Production method: Take the above-mentioned raw materials, add water, hydroxypropyl methylcellulose, water repellent, styrene-acrylic emulsion and film-forming aids into the mixer and stir evenly; slowly add Shuangfei powder and ash calcium powder Blender until smooth to a paste.

Embodiment approach 2

[0016] Take 650 parts of Shuangfei powder; 155 parts of ash calcium powder; 5.2 parts of hydroxypropyl methylcellulose; 195 parts of water; 75 parts of nano water repellent;

[0017] Production method: Take the above-mentioned raw materials, add water, hydroxypropyl methylcellulose, water repellent, styrene-acrylic emulsion and film-forming aids into the mixer and stir evenly; slowly add Shuangfei powder and ash calcium powder Blender until smooth to a paste.

[0018] In order to facilitate preservation, especially in summer, a bactericidal preservative can be added on the basis of the above-mentioned ingredients, and the specific implementation method is as follows:

Embodiment approach 3

[0020] Get 500 parts of Shuangfei powder; 110 parts of ash calcium powder; 4.1 parts of hydroxypropyl methylcellulose; 160 parts of water; 55 parts of nano water repellent; The weight fraction is 0.8 parts.

[0021] Production method: Take the above-mentioned raw materials, add them into the mixer in the order of water, hydroxypropyl methylcellulose, water repellent, styrene-acrylic emulsion, film-forming aids, and bactericidal preservatives and stir evenly; mix Shuangfei powder and ash calcium Slowly add the powder into the blender and mix until it becomes a paste.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a multiple-effect putty paint, which comprises the following raw materials (by weight ratio): Talcum powder 500-650 parts, ash calcium powder 110-155 parts, methylcellulose propylene glycol ether 4.1-5.2 parts, water 160-195 parts, nano water-repellent admixture 55-75 parts, styrene / acrylic emulsion 85-100 parts and film forming adjuvant 2.4-3.3 parts.

Description

technical field [0001] The invention relates to a multi-effect putty paint for wall painting. Background technique [0002] The materials used to decorate the wall are imitation porcelain paint and latex paint. The general imitation porcelain paint is not water-resistant, has poor hardness, is easy to powder, and is easy to age. The better imitation porcelain tempered paint in the imitation porcelain paint has high hardness Yes, but the washing resistance is poor and the color is single. In addition, the imitation porcelain coating has relatively high requirements in the construction process. The construction methods of polyurethane imitation porcelain coating, silicone acrylic resin imitation porcelain coating and water-soluble polyvinyl alcohol imitation porcelain coating are not the same. , need to be strictly distinguished, and no matter what kind of coating construction method, the construction requirements environment and difficulty are relatively large; while the wate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/34
Inventor 王明喜
Owner 王明喜
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com