Improved composite high-chromium iron-cast roller

A technology of high-chromium cast iron and rolls, which is applied in the field of improved composite high-chromium cast iron rolls, which can solve the problems of reduced surface quality of rolled strips, thermal cracks in the working layer of high-chromium cast iron, easy peeling of oxide film, etc., and achieve rolling output The effect of improving, increasing service life and reducing large inclusions

Active Publication Date: 2006-11-01
JIANGSU GONGCHANG ROLL
View PDF0 Cites 16 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing composite high-chromium cast iron rolls not only produce thermal cracks in the high-chromium cast iron working layer, but also easily peel off the oxide film produced on the roll surface during the rolling process, so the existing composite high-chromium cast iron rolls have poor wear resistance. In addition, the peeling of the oxide film on the roll surface will also lead to a decrease in the surface quality of the rolled strip

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Improved composite high-chromium iron-cast roller
  • Improved composite high-chromium iron-cast roller

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Example 1: According to the composition of the high chromium cast iron working layer, put the proportioned pig iron, scrap and high chromium cast iron into the intermediate frequency furnace for smelting. After smelting, the chemical composition of the original molten iron is analyzed, and then the corresponding alloy material is added. The composition obtained by smelting is C2.6%WT, Si0.9%, Mn0.7%, Ni1.2%, Cr15%, Mo1.5%, V0.25%, W0.6%, N0.05%, Al0. 1%, P≤0.04%, S≤0.04%, the rest is molten iron in the working layer of iron and impurities, centrifugal cast composite rolls. After heat treatment, the hardness of the working layer of the roll is 78HSD, the tensile strength of the working layer is 830Mpa, and the unevenness of the working layer hardness is less than 2HSD. After the rolling test, the grinding volume of each roll is less than 0.15mm, and the millimeter rolling volume is 50% higher than that of the roll with the original working layer of high chromium cast iron.

Embodiment 2

[0014] Embodiment 2: As in embodiment 1, the composition of the working layer of the roll is C2.8%, Si1.0%, Mn0.9%, Ni1.4%, Cr18%, Mo3.0%, V0.4%, W1.0 %, N0.07%, Al0.2%, P≤0.04%, S≤0.04%, the rest is iron and impurities. After the composite roll is heat-treated, the hardness of the working layer is 88HSD, the tensile strength of the working layer is 850Mpa, and the unevenness of the working layer hardness is less than 2.5HSD. After the rolling test, the grinding volume of each roll is less than 0.15mm, and the millimeter rolling volume is 60% higher than that of the roll with the original working layer of high chromium cast iron.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to view more

Abstract

It is a type of complex high-chromium green roll with strong oxidation resistance and wearable property. Components of its working lining are as follows: 2.5-3.0% C,0.5-1.2% Si,0.6-1.2% Mn,1.0-1.5% Ni,12-20% Cr,0.5-3.5 % Mo,0.05-0.5% V,0.2-1.5% W,0.03-0.3% Al, 0.03-0.1% N ,P <=0.04%,S <=0.04%,iron and impurity the rest. Advantages of this kind of green roll are as follows: wear-resisting property was improved by 50% ,mm rolling quantity increased by 30%,its life-span and rolling output were doubled, draw resistent intensity was reinforced and rigidity asymmetry was lowered effectively.

Description

Technical field [0001] The invention relates to an improvement of a hot-rolled strip steel composite high-chromium cast iron roll, in particular to a composite high-chromium cast iron roll with strong oxidation resistance and high wear resistance. Background technique [0002] The composite high-chromium cast iron roll used in the front section of the hot-rolled strip continuous rolling machine for finishing rolling, the roll surface will produce an oxide film during the rolling process. This oxide film has high strength and wear resistance, so it can protect the roll surface. Improve the wear resistance of the roll surface and reduce wear. However, the existing composite high chromium cast iron rolls not only produce hot cracks in the high chromium cast iron working layer, but also the oxide film produced on the roll surface is easily peeled off during the rolling process. Therefore, the existing composite high chromium cast iron rolls have poor wear resistance. High consumption...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C22C38/56
Inventor 张文君邵顺才步小平
Owner JIANGSU GONGCHANG ROLL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap