Production of coating fabrics with high-peneration and waterproofing functions

A technology of waterproof coating and manufacturing method, which is applied in the direction of textiles and papermaking, can solve the problems of complicated process and long drying time of water-emulsion coating agent, and achieve broad sales prospects, excellent water resistance and good moisture permeability Effect

Inactive Publication Date: 2007-04-04
TORAY FIBER RES INST(CHINA) CO LTD
View PDF0 Cites 44 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the water-emulsion coating agent takes a long time to dry and needs to be baked, and the process is more complicated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A method for manufacturing a high moisture-permeable and highly waterproof coated fabric, comprising the following steps:

[0023] ① Mix the following components by weight to form a fabric coating agent:

[0024] Polyurethane polymer 100 parts

[0025] Polar solvent butanone (or methyl isobutyl ketone, isopropanol) 50 parts

[0026] Non-polar solvent benzene (or toluene, xylene) 50 parts

[0027] Water repellant 4 parts

[0028] 9 parts of film former

[0029] Cross-linking agent 2 parts

[0030] slip agent 4 parts

[0031] 90 parts of water;

[0032] ②Apply the prepared fabric coating agent evenly on the base cloth to form a coating, and put the coating into an oven for drying treatment before the fabric coating agent is dry. The drying treatment temperature is 50-150°C (for example 50°C, 100°C, 150°C), the processing time is 30 seconds to 3 minutes (eg 30 seconds, 1 minute, 2.5 minutes, 3 minutes).

[0033] After step 2. drying treatment, also carry out post-d...

Embodiment 2

[0045] The weight component that is mixed into fabric coating agent is:

[0046] Hydrophilic polyurethane polymer 100 parts

[0047] Polar solvent butanone (or methyl isobutyl ketone, isopropanol) 40 parts

[0048] 40 parts of non-polar solvent benzene (or toluene, xylene)

[0049] Water repellant 8 parts

[0050] Film forming agent 6 parts

[0051] 1 part of cross-linking agent

[0052] slip agent 10 parts

[0053] Brightener 10 parts

[0054] 130 parts of water;

[0055] Wherein the whitening powder adopts the whitening agent of conventional coating fabrics such as titanium dioxide, the X-2093 product that example Dainichi Seika Industry Co., Ltd. produces) all the other are with embodiment 1.

[0056] project

Embodiment 3

[0057] Embodiment 3: the weight component that is mixed into fabric coating agent is:

[0058] Hydrophilic polyurethane polymer 100 parts

[0059] Polar solvent butanone (or methyl isobutyl ketone, isopropanol) 60 parts

[0060] 60 parts of non-polar solvent benzene (or toluene, xylene)

[0061]Water repellant 2 parts

[0062] Film forming agent 15 parts

[0063] 3 parts of cross-linking agent

[0064] 70 parts of water;

[0065] All the other are with embodiment 1.

[0066] project

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

This invention was a public high permeability high waterproof coating fabrics manufacturing methods, including polyurethane polymer, an organic solvent, allocation of water, as agent, crosslinking agents, other agents, water mixed into a fabric coating agents will be made of fabric coated with the coating in uniform as coating on the fabric, Fabric coating agent had dried occasion of the coating for drying processing steps. The invention manufactured coated fabric is not only an excellent waterproof and good moisture permeability but also has good rubbing sex and the feeling of fullness soft features. Product hydrostatic pressure 5000mm H2O over Al permeability to 8000g / m2 . 24hr above Tolerance washing and rubbing. Such coated fabric has broad prospects for sales, which can be used to produce rainwear, breathable, ski clothes, cool suits. Have greater economic and social benefits.

Description

Technical field: [0001] The present invention relates to a method for the manufacture of coated fabrics. Background technique: [0002] The existing waterproof and moisture-permeable coated fabric is made by uniformly coating the polyurethane polymer coating finishing agent on the fabric to form a layer of porous film on the surface of the fabric. [0003] Commonly used polymer coating finishing agents are solvent-based and water-emulsion-based. Solvent-based coating finishing agent has the characteristics of easy drying and tough and glossy coating film, but the pollution is serious and the cost is high. The water-emulsion coating agent uses water as the medium, which has the characteristics of no pollution to the environment and low cost. However, the water-emulsion coating agent takes a long time to dry and needs to be baked, and the process is more complicated. All in all, both types of coating agents have their advantages and disadvantages. [0004] As we all know, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/12
Inventor 袁小飞石井正树稻田康二郎
Owner TORAY FIBER RES INST(CHINA) CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com