Method for preparing solvent-type organosilicon waterproof liquid

A manufacturing method and silicone technology, applied in chemical instruments and methods, other chemical processes, etc., can solve problems such as difficulties, small penetration depth of waterproofing agent, and failure to achieve overcoating effect, etc., to achieve good weather resistance and strong permeability , good effect

Inactive Publication Date: 2007-05-16
陈俊光
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The biggest disadvantage of these waterproofing agents is that after using one type of silicone waterproofing agent, it is very difficult to add another type of waterproofing agent, and the overcoating effect cannot be achieved.
Moreover, the penetration depth of the waterproofing agent in the base material is small, and the waterproofing effect will be lost after a certain period of natural aging.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] Add heptadecafluorooctylethylenetrimethoxysilane into the stirrer and stir evenly, then pass through N 2 20 minutes at N 2 Keep adding isopropanol and mix for 20 minutes to form a pre-mixture; stir the pre-mixture for 0.5 hours to carry out aging reaction, and then package it under nitrogen protection to obtain a solvent-based silicone waterproof liquid with a surface dry time of 0.5 hours. The consumption of above-mentioned each component is as follows:

[0016] Heptadecafluorooctylethylenetrimethoxysilane 15g

[0017] Isopropanol 85g.

Embodiment 2

[0019] Add heptadecafluorooctylethylenetrimethoxysilane into the stirrer and stir evenly, then pass through N 2 25 minutes at N 2 Keep adding isopropanol and mix for 25 minutes to form a pre-mixture; stir the pre-mixture for 0.6 hours to carry out aging reaction, and then package it under nitrogen protection to obtain a solvent-based silicone waterproof liquid with a surface-drying time of 0.5 hours. The consumption of above-mentioned each component is as follows:

[0020] Heptadecafluorooctylethylenetrimethoxysilane 1g

[0021] Isopropanol 97g.

Embodiment 3

[0023] Add octyltriethoxysilane to the stirrer and stir evenly, then pass N 2 35 minutes at N 2 Keep adding isopropanol and mix for 35 minutes to form a pre-mixture; stir the pre-mixture for 0.7 hours to carry out aging reaction, and then package it under nitrogen protection to obtain a solvent-based silicone waterproof liquid with a surface-drying time of 0.5 hours. The consumption of above-mentioned each component is as follows:

[0024] Octyltriethoxysilane 99g

[0025] Isopropanol 1g.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparing method of solvent-typed organic silicon water-proof liquid, which comprises the following steps: blending active organic silicane, active organic silicon oil and active organic silicon resin to stir evenly; aerating N2 for 20-40min; adding organic solvent under N2 to mix 20-40min; adding catalyst; forming pre-mixture; stirring the premixture for 0.5-1h to age; packing protected by nitrogen to obtain the product.

Description

technical field [0001] The invention relates to a method for manufacturing a solvent-based silicone waterproof liquid used for waterproofing treatment of porous substrates. Background technique [0002] Existing silicone waterproofing agents are water-based, paste, emulsion and powder. The biggest disadvantage of these waterproofing agents is that after using one type of silicone waterproofing agent, it is very difficult to add another type of waterproofing agent, and the overcoating effect cannot be achieved. Moreover, the penetration depth of the waterproofing agent in the base material is small, and the waterproofing effect will be lost after a certain period of natural aging. With the improvement of environmental protection requirements, the solvents of decorative materials cannot contain substances that are toxic to human health and pollute the environment. For the convenience of construction, it is required to choose different solvent types according to the change of...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09K3/18C08L83/04C08K5/54
Inventor 陈俊光
Owner 陈俊光
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com