Ceramic sintering fluxing agent

A technology of flux and ceramics, which is applied in the field of building materials, can solve the problems of high energy consumption, achieve the effects of lower firing temperature, low price, and easy promotion

Inactive Publication Date: 2007-06-06
UNIV OF SCI & TECH BEIJING
View PDF0 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the problem of high energy consumption in the firing process of materials, the present invention proposes a new type of fluxing method aimed at reducing the firing temperature of materials—gradual local fluxing method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic sintering fluxing agent

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] 1. A ceramic firing flux containing 35% B by mass fraction 2 o 3 , K with a mass fraction of 30% 2 O+Na 2 O, mass fraction is 35% CaF 2 ;

[0025] 2. A ceramic firing flux containing 25% B by mass fraction 2 o 3 , K with a mass fraction of 35% 2 O+Na 2 O, mass fraction is 40% CaF 2 ;

[0026] 3. A ceramic firing flux containing 30% B by mass fraction 2 o 3 , K with a mass fraction of 28% 2 O+Na 2 O, mass fraction is 42% CaF 2 ;

[0027] 4. A ceramic firing flux containing 24% B by mass fraction 2 o 3 , PbO with a mass fraction of 40%, CaF with a mass fraction of 36% 2 ;

[0028] 5. A ceramic firing flux containing 20% ​​B by mass fraction 2 o 3 , PbO with a mass fraction of 49%, CaF with a mass fraction of 31% 2 ;

[0029] 6. A ceramic firing flux containing 27% B by mass fraction 2 o 3 , PbO with a mass fraction of 45%, and CaF with a mass fraction of 28% 2 ;

[0030] 7. A ceramic firing flux containing 25% V by mass fraction 2 o 5 , Bi with...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention is ceramic sintering fluxing agent, and belongs to the field of building material technology. The method of the present invention is that the first level fluxing agent capable of generating solid solution of lower smelting point is used in fluxing the second level fluxing agent capable of generating solid solution of higher smelting point, the second level fluxing agent is used in fluxing the third level fluxing agent, and so on to complete the sintering of the material at relatively low temperature and lowered power consumption. The ceramic sintering fluxing agent of the present invention is a composite fluxing agent comprising B2O3, K2O+Na2O and CaF2 separately as the first level, the second level and the third level fluxing agent, or comprising Bi2O3, PbO and CaF2, or comprising V2O5, Bi2O3 and LiF+AlF3. It is added into sintering process in the amount of 0.01-0.5 % to lower the sintering temperature by 100 -170 deg.c.

Description

technical field [0001] The invention belongs to the field of building materials, in particular to a ceramic firing flux. technical background [0002] As an important production department in the building materials industry, the firing process of ceramic products is characterized by high temperature and high energy consumption. The most fundamental way to reduce energy consumption in the firing process is to significantly reduce the firing temperature of materials. At present, there are two main ways to reduce the firing temperature: (1) Grinding the fired raw materials into ultra-fine powders with very small particle sizes, some of which are ground to submicron or nanometer levels, greatly increasing the contact of raw materials The surface area increases the total surface energy of the raw material, thereby strengthening the firing process of the material; (2) By adding a compound with a single fluxing effect, it forms a low melting point solid solution with the main raw ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/63C04B35/64
Inventor 夏德宏邓娜邬传谷
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com