Ecological nano enamel paint

A nano and enamel technology, applied in the field of building interior wall coatings, can solve the problems of inconvenience, corrosion resistance, water resistance, etc., and achieve the effects of simple production, strong adhesion, and excellent alkali resistance.

Inactive Publication Date: 2007-06-13
BEIJING HONGMENG BUILDING MATERIAL TECH INST
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, there are many interior wall coatings on the market, such as putty powder, which mainly have the following defects in application: 1. The strength is poor, not wear-resistant, easy to fall off, not water-resistant and easy to mildew, and some are not corrosion-resistant, so More or less high-quality coatings will bring great inconvenience to construction and home life

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Ecological nano enamel, containing the following ratio of raw materials:

[0022] White cement 425 # : 21%, Calcium Hydroxide: 28%,

[0023] Talc: 12%, Ground Calcium Carbonate: 18%,

[0024] Titanium dioxide: 19.5%, methyl cellulose: 2‰,

[0025] Neutral nano-hydrophobic agent: 4‰, methyl hydroxyethyl cellulose: 5‰,

[0026] MCP801 rubber powder: 4‰

[0027] Wherein, the fineness of talcum powder is: 800 mesh, and the whiteness is: 95 degrees; the fineness of heavy calcium carbonate is: 800 mesh, and the whiteness is: 93 degrees; the viscosity of the methyl cellulose is 80,000 centipoise ; The viscosity of the methyl hydroxyethyl cellulose is: 50,000 centipoise;

Embodiment 2

[0029] Ecological nano enamel, containing the following ratio of raw materials:

[0030] White cement 425 # : 40%, Calcium Hydroxide: 15%,

[0031] Talc: 13%, Ground Calcium Carbonate: 15%,

[0032] Titanium dioxide: 15.5%, methyl cellulose: 1.5‰,

[0033] Neutral nano-hydrophobic agent: 5‰, methyl hydroxyethyl cellulose: 3‰,

[0034] MCP801 rubber powder: 5.5‰

[0035] Among them, the fineness of talcum powder is: 600 mesh, and the whiteness is: 90 degrees; the fineness of heavy calcium carbonate is: 550 mesh, and the whiteness is: 92 degrees; the viscosity of the methyl cellulose is 35,000 centipoise ; The viscosity of the methyl hydroxyethyl cellulose is: 55,000 centipoise.

[0036] For the ecological nano-enamel paint of the present invention, raw materials with corresponding proportions can be added into the container and stirred evenly with a mixer.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
whitenessaaaaaaaaaa
whitenessaaaaaaaaaa
whitenessaaaaaaaaaa
Login to View More

Abstract

This invention discloses a kind of ecological nano enamel lacquer containing crude materials white the following mixture ratios: 10~60% of white cement 425#, 10~60% of calcium hydroxide, 10~50% of talcum powder, 10~50% of heavy calcium carbonate, 15~50% titanium white powder, 15~40% methyl cellulose, 0.2-10%. of neutral nano hydrophobing agent, 3-15%. of carboxymethyl hydroxyetheyl cellulose 0.2-10%. of MCP801, 0.2-10%. of rubber powder. The said ecological nano enamel lacquer in this invention is characteristic of high strength, crack resistance, corrosion resistance, scrub resistance and simple construction.

Description

technical field [0001] The invention relates to a building interior wall coating, in particular to an ecological nano-enamel paint. Background technique [0002] At present, there are many interior wall coatings on the market, such as putty powder, which mainly have the following defects in application: 1. The strength is poor, not wear-resistant, easy to fall off, not water-resistant and easy to mildew, and some are not corrosion-resistant, so High-quality paint will more or less bring great inconvenience to construction and home life. Contents of the invention [0003] The invention solves the technical problems existing in the prior art, and provides an ecological nanometer enamel paint with high strength, crack resistance, corrosion resistance, scrub resistance and simple construction. [0004] In order to achieve the above object, the technical scheme that the present invention takes is: [0005] A kind of ecological nano-enamel paint, comprises the raw material of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D101/26C09D5/28
Inventor 饶和泰
Owner BEIJING HONGMENG BUILDING MATERIAL TECH INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com