Protective coating

a technology of protective coating and film, applied in the direction of temporary coating, cellulose derivative coating, starch coating, etc., can solve the problems of inter alia water resistance destruction of the film properties of the coating

Inactive Publication Date: 2006-09-14
POLYSACCHARIDE INDS PSI
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

[0010] Another object of the invention is to provide a coating system for the protection of substrates selected from vehicles, such as cars, trains and air crafts, architectural structures, under-water structures obtaining anti-fouling properties, conifer seedlings for protection against insecticidal or microbial attack, and silver or copper articles for protection against oxidation or other types of discolouring.

Problems solved by technology

In order to develop the polysaccharide coating that can resist high concentrations of acid influence it was experienced that the high concentrations of buffering salts that were necessary to build high buffering capacity resulted in destruction of the film properties of the coating in regard to inter alia water resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0045] To an aqueous solution containing 0.375% (w / v) of locust bean gum and 1.125% (w / v) of guar gum was added Lupasol SK, MW 2000 000 (BASF), to give a final concentration of 1.8% (w / v). The mixture was thoroughly mixed and the pH adjusted to 8. The resulting viscous solution was applied to lacquered test plates (0.5 L / m2).

[0046] Three methods of drying were used: [0047] 1. Forced drying in an oven at 70° C. for 20 min. [0048] 2. Forced drying using infrared heater for 10 min. [0049] 3. Drying in room temperature for 20 hrs.

[0050] The coating dried at elevated temperatures (1 and 2) and became very tough and were scratch resistant.

[0051] Showering the coatings with water at room temperature for 1 hour resulted in some swelling of the coatings (most apparent on the coating dried by method 3. but the coatings were essentially resistant to this water exposure at room temperature.

[0052] The coatings were tested according to test recommendations from Volvo AB including test with 1%...

example 2

[0054] The galactomannans guar gum and locust bean gum in the proportions 75:25 (w / w) were dissolved in water (2.2% at 90° C. and allowed to cool to 40° C. To the resulting solution was added polyethylenimine, Lupasol P, MW 750 000 (BASF) in a concentration of 3.6% (w / v). After careful mixing, the pH was adjusted to 8.0 by the addition of acetic acid. The resulting solution was sprayed on a lacquered metal surface (0.3 l / m2) and allowed to dry. During the drying process the solution changed into gel before forming a film. Using the experimental procedure as in Example 1 similar results were obtained.

example 3

[0055] To an aqueous solution of 1.5% (w / v) of locust bean gum was added Lupasol P to a final concentration of 1.2% (w / v) and the mixture was thoroughly mixed. The pH of the solution was adjusted to 12. The resulting solution was applied to solution to lacquered test plates (0.25 L / m2) and immersed into coastal waters at the East and West Coast of Sweden. After 3 months the test plates were inspected for barnacle and algae growth and it was found that the growth of these organisms was significantly reduced. The dirt that had accumulated and the coating could easily be removed by high-pressure water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
temperaturesaaaaaaaaaa
pressureaaaaaaaaaa
pressureaaaaaaaaaa
Login to View More

Abstract

A composition is provided consisting of an aqueous solution comprising at least one natural polysaccharide or a derivative thereof and at least one polymeric polyamino compound, the composition being capable of forming a film when applied onto a substrate. The invention also involves a method for temporary protection of a substrate surface from environmental influence using such composition.

Description

[0001] This is a Continuation of U.S. patent application Ser. No. 10 / 472,949, filed Mar. 1, 2004, which is a filing under 35 U.S.C. §371 of International Patent Application No. PCT / SE02 / 00600, filed Mar. 27, 2002, and the benefit is claimed under 35 U.S.C. §119(a)-(d) of Swedish Application No. 0101096-6, filed Mar. 28, 2001.FIELD OF THE INVENTION [0002] The present invention relates to compositions in the form of aqueous solutions containing at least one natural polysaccharide or derivatives thereof and at least one polymeric polyamino compound. The invention also covers a method for temporary protection of a substrate surface from environmental influence using such compositions. BACKGROUND OF THE INVENTION [0003] Non-toxic and environmentally safe protective coatings are being developed in order to replace presently used systems, which are based on products which are encountered with toxicological and environmental draw-backs, such as acrylics, urethanes and epoxy polymers manufac...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(United States)
IPC IPC(8): A61K8/73C09D101/18C09J103/02C08L5/08C08L89/00C09D101/00C09D5/00C09D5/20C09D105/14C09D157/12C09D185/00C09D189/00
CPCC09D5/008C09D105/14C08L2666/02C09D101/08
Inventor SVENSSON, SIGFRID
Owner POLYSACCHARIDE INDS PSI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com