Biodegradable resin composition
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Benefits of technology
Problems solved by technology
Method used
Image
Examples
Example
Example 1
[0045] After 70 parts by weight of cellulose diacetate having a molecular weight of 202,332 (Eastman Co., Ltd.), and 30 parts by weight of triacetin (Mw. 218.21, major component C9H14O6), Dae Shin Chemical Ind. Co., Ltd.) as a plasticizer were evenly mixed, the mixture was kneaded for 3 hours at the temperature of 100° C. and melted in Haake rheocord system of 200° C. thereby to prepare a blending mixture.
Example
Examples 2 to 8 and Comparative Examples 1 to 6
[0046] With the exception that the compositions and ratios as shown in Table 1 below were used, blending mixtures were prepared by carrying out the same method as above Example 1. TABLE 1Cellulose(Parts byPlasticizerWeight)TATECGCESOBETEX. 1CDA1 7030EX. 2CDA1 8020EX. 3CDA1 8020EX. 4CDA1 8020EX. 5CDA1 801010EX. 6CDA2 8020EX. 7CDA2 702010EX. 8CDA3 8020EX. 9CDA3 7030COM. EX. 1CA 9010COM. EX. 2CA 8020COM. EX. 3CA 7030COM. EX. 4pure PPCOM. EX. 5pure PLA
Note
CDA1: Cellulose (Di)Acetate(Mn ca. 202,332 g · mol−1, 54.5 wt. % acetyl content, Tg 188° C., Eastman Co., Ltd)
CDA2: Recycling fabric CDA (SK)
CDA3: Recycling fiber CDA (SK)
CA: Cellulose acetate(Mn ca. 50,000 g · mol−1, 39.7 wt. % acetyl content, Tg 188° C., Aldrich Co., Ltd.)
PP: Polypropylene (grade H1500, Hyundai)
PLA: Polylacetic acid (Mn 83,000 g · mol−1 , Mw 153000 g · mol−1 Cargill-Dow Co., Ltd.)
TA: Triacetin(Mw. 218.21), Dae Shin Chemical Ind. Co., Ltd.
TEC: Triethyl citrate(M...
Example
[0052]FIG. 1 showed the biodegradability of Example 2 of the invention and cellulose which is a standard material over time and FIG. 2 showed the biodegradability of Comparative Example 5 and the cellulose which is a standard material over time.
[0053] As shown in FIG. 1 and FIG. 2, the biodegradable resin composition of the invention showed biodegradability almost equal to that of Comparative Example 5 wherein the commonly used biodegradable resin composition was used.
[0054] The biodegradable resin composition in accordance with the invention can remarkably lower the manufacturing costs when compared with the cellulose acetate which has been used as biodegradable plastic materials, can prevent environmental contamination by reusing the cause factor of environmental contamination, remarkably improves the properties, is easy to be prepared into moldings at a low temperature due to its low melting point, and has considerably improved properties when compared with prior biodegradable ...
PUM
Property | Measurement | Unit |
---|---|---|
Percent by mass | aaaaa | aaaaa |
Percent by mass | aaaaa | aaaaa |
Mass | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap