High-performance ceramic surface metallization process

A metallization treatment and ceramic surface technology, applied in the field of ceramic surface metallization treatment process, can solve the problem of affecting the welding strength and airtightness of metallized ceramics and metal, without considering the influence of the quality of the metallized layer, and uneven thickness of the metallized layer and other problems, to achieve the effect of good air tightness, easy operation and high pass rate of product quality

Inactive Publication Date: 2009-12-16
湖南湘瓷科艺有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, in the ceramic metallization process, the quality of the metallization layer is only improved by controlling the viscosity of the metal paste and the temperature of the processing environment, without considering the influence of the workpiece itself on the quality of the metallization layer due to changes in the environment and weather
Therefore, the printed workpiece is prone to defects such as pinholes, paste accumulation, uneven thickness and cracking of the metallization layer, paste flow around, and foreign matter sticking, which will affect the strength and airtightness of the final metallized ceramic and metal welding.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0014] A ceramic surface metallization treatment process, which includes ultrasonic cleaning of ceramic workpieces - calcination - automatic printing - metallization sintering - electroplating and nickelization sintering processes, characterized in that the ceramic surface metallization treatment is After the ceramic workpiece is calcined and before automatic printing, an infrared heating pretreatment process is added to the ceramic workpiece, that is, after the ceramic workpiece is calcined, the ceramic workpiece is placed in an automatic transmission infrared heating device for infrared heating. The processing time is 5-30 minutes, the temperature in the heating device is controlled between 40°C-100°C, and the outlet temperature of the workpiece is controlled at 60-100°C. After the infrared heating pretreatment, the ceramics are automatically coated with metal paste. , the metal paste with a certain viscosity can flow quickly and evenly on its surface, and can quickly form a ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a high-performance ceramic surface metallization processing technique comprising ultrasonic cleaning, calcining, infrared heating, automatic coating and printing, metalized agglutination, and galvanization and nickel agglutination. The invention is a technique that carries infrared pre-heating treatment on the ceramic surface to be metalized, automatically coats and prints the metal ointment to form an evenly dense flat metallization layer. The invention belongs to one of the techniques for improving the surface function of the high-performance compound ceramics. The metal ceramics which is produced with the technique can be welded with metal to form the high-performance compound ceramic ware which is featured by firm connection, good airproof and reliable quality and is widely applied in the fields of vacuum electronic devices, spaceflight, aviation, broadcast TV, communication, metallurgy, medicine, high energy physics, etc. The technique is easily operated and controlled, and the product has high good yield, thereby greatly reducing the loss cost of the noble metal and significantly improving the production efficiency.

Description

technical field [0001] The invention relates to a ceramic surface metallization treatment process. Background technique [0002] In the current ceramic metallization process, the quality of the metallization layer is only improved by controlling the viscosity of the metal paste and the temperature of the processing environment, without considering the impact of the workpiece itself on the quality of the metallization layer due to changes in the environment and weather. Therefore, the printed workpiece is prone to defects such as pinholes, paste accumulation, uneven thickness and cracking of the metallization layer, paste flow around, and foreign matter sticking, which will affect the strength and airtightness of the final metallized ceramic and metal welding. Contents of the invention [0003] The purpose of the present invention is to overcome the above disadvantages, to provide a method of increasing the infrared heating pretreatment on the surface of ceramic workpieces,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C04B41/88
Inventor 杨子初陈金华李微刘秋生程文琴邹建平
Owner 湖南湘瓷科艺有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products