Concrete water-permeable brick using steel slag as aggregate

A permeable brick and concrete technology, applied in the field of building materials, can solve the problems of waste of resources and environment, high energy consumption, low water permeability, etc., and achieve the effect of strong pressure resistance and low energy consumption

Inactive Publication Date: 2007-08-01
SUZHOU HUAJIA NEW BUILDING
View PDF0 Cites 44 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, the common pavement permeable bricks are roughly divided into sintered ceramic permeable bricks and cement permeable bricks. However, sintered ceramic permeable bricks have high cost and high energy consumption, and cannot be widely promoted at present, while cement permeable bricks either have low water permeability. Either the water permeability is good, but the compressive strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0018] A concrete permeable brick using steel slag as an aggregate is made of steel slag, cement, reinforcing agent, coloring powder and water as raw materials according to the following formula.

[0019] Raw material specification dosage (kg)

[0020] Portland cement C52.5 conch 350

[0021] High quality inorganic pigment Bayer 0~10.5

[0022] Ethylene polymer polymer emulsion Solid content 40% 1.75~21

[0023] Steel slag 1~3mm 150~300

[0024] Steel slag 5~8mm 1450~1600

[0025] Water Tap water 90~100

[0026] The method for producing steel slag concrete permeable bricks is carried out according to the following steps:

[0027] material selection

[0028] Thermally purify and adjust the waste steel slag to reduce the content of free calcium oxide in the steel slag to less than 3%, and the crushing value is less than 5%. Then, the scrap steel slag is crushed and classified into two specifications of 1-3mm and 5-8mm for use ;

[0029] Cement, C52.5 low-alkali cement is...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Water permeability coefficientaaaaaaaaaa
Login to view more

Abstract

The invention discloses a concrete permeable brick of steel slag as aggregate, which comprises the following steps: allocating raw material with 70-85% steel slag with grinding value less than 5% and free calcium oxide less than 3%, 10-25% C52.5 low-alkaline cement, 0.5-6% reinforcer, 0-3% coloring powder and 3.5-5% water; blending raw materials in the mixer; distributing; molding; obtaining the product.

Description

technical field [0001] The invention belongs to the field of building materials, in particular to a permeable road brick formed by pressing waste steel slag and cement at normal temperature. Background technique [0002] At present, the common pavement permeable bricks are roughly divided into sintered ceramic permeable bricks and cement permeable bricks. However, sintered ceramic permeable bricks have high cost and high energy consumption, and cannot be widely promoted at present, while cement permeable bricks either have low water permeability. Either the water permeability is good, but the compressive strength is not high. It is difficult to balance the performance of these two aspects. Steel slag is a kind of metallurgical solid waste that is currently difficult to use with high added value. At present, a large amount of waste slag produced by steelmaking in major iron and steel plants in my country cannot be disposed of. , long-term land occupation, waste of resources and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/00C04B18/14
CPCC04B2111/00284C04B2111/00017C04B28/02Y02W30/91C04B16/0641C04B18/142C04B40/0028
Inventor 钱卫胜
Owner SUZHOU HUAJIA NEW BUILDING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap