Jet ink liquid for color filter, manufacturing method for color filter, color filter and displaying device
A manufacturing method and technology of color filters, applied in the direction of copying/marking methods, optical filters, inks, etc., can solve the problems of uneven pixel color, ink wetting and expansion may not be the same, etc., to achieve the suppression of color unevenness, suppression Extended variation, good flatness effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0126] [Production of color filter and display device]
[0127] [Color filter]
[0128] -Preparation of deep color composition for partition wall formation-
[0129] The concentrated color composition K1 can be obtained as follows: First, measure the K pigment dispersion 1, propylene glycol monomethyl ether acetate in the amount shown in Table 1, and mix at a temperature of 24°C (±2°C) , Stir at 150rpm for 10 minutes, then measure the amount shown in Table 1 of methyl ethyl ketone, binder 2, hydroquinone monomethyl ether, DPHA liquid, 2,4-bis(trichloromethyl) -6-[4'-(N,N-bisethoxycarbonylmethyl)amino-3'-bromophenyl]-s-triazine, surfactant 1, at a temperature of 25°C (±2°C) Then, the mixture was added sequentially, and the resulting material was stirred at 150 rpm at a temperature of 40°C (± 2°C) for 30 minutes. In addition, the amounts shown in Table 1 are parts by mass, and are specifically the following composition.
[0130]
[0131] ·Carbon black (Nipex35 manufactured by デグツサ)...
Embodiment 2~4、 comparative example 1~3
[0190] In Example 1, except that the polymerizable monomer in the ink was changed to the polymerizable monomer described in Table 4, a color filter and a liquid crystal display device were produced in the same manner as in Example 1.
[0191] The viscosity of the polymerizable monomer at 25°C was measured using a viscometer (B-type viscometer, manufactured by Toki Co., Ltd.).
[0192]
Embodiment 5~6
[0194] In Example 1, the pigment dispersion liquid (G1) for G was changed to (G3) or (G5) described in Table 5 below, and (G2) was changed to (G4) or (G6). In the same manner as in Example 1, a color filter and a liquid crystal display device were produced.
[0195] In addition, for PG36 pigment dispersions (G3) and (G5), different batches of G pigment dispersions (G3A) to (G3E) and (G5A) to (G5E) were prepared in the same manner as in Example 1. Color filters and liquid crystal display devices.
[0196]
[0197](Parts by mass)
PUM
Property | Measurement | Unit |
---|---|---|
Boiling point | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com