Novel process for leather retanning

A new technology and leather technology, applied in the field of leather making, can solve the problems of large water consumption, land occupation, high power consumption, etc., achieve high concentration, good compatibility, and overcome tight surface knots

Active Publication Date: 2010-05-26
鹤山腾泰皮革有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There are following technical defects in the above-mentioned prior art: 1. produce a large amount of chromium-containing wastes---chrome leather shavings in the smoothing process, and only my country just produces about 280,000 tons of chromium-containing wastes every year, and the most suitable for chrome leather shavings at present The best treatment method is to landfill it, which not only occupies land resources, but also brings environmental pollution; 2. This process produces a large amount of industrial wastewater, the pH of which is 8-10, and the suspended solids are 3000mg / l. Cr 3+ The content is 60~100mg / l, COD Cr 2000~3000mg / l, S 2- (Iodometric method) content of 100 ~ 200mg / l, BOD 5 2200mg / l, Cl - It is 3000mg / l, causing serious pollution to rivers and farmland in my country; 3. The whole process consumes a lot of water, consumes a lot of electric energy, has a long process cycle and high cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] Preparation of lignin protein filled retanning agent:

[0030] First, add 0-140 parts by mass of water, 270 parts of chrome leather shavings and 65 parts of sodium hydroxide into the reactor, stir for 5 minutes, add the second part of 270 parts of chrome leather shavings and 60 parts of sodium hydroxide , stirred for 5 minutes, then added 270 parts of chrome leather shavings and 60 parts of sodium hydroxide in the third part, stirred for 20 minutes, and the reactant was a uniform paste. Add 72 parts of ammonium lignosulfonate, and continue stirring for 12 hours. Then 55 parts of formic acid are added dropwise in a trickle, and the control time is 3 hours, and 100 parts of sulfuric acid are added dropwise in a trickle, and the control time is 3 hours. Check the pH value of the 1:10 aqueous solution of the reactants to be 7.5 to 8.0. It should be noted that the specific amount of water depends on the dryness and wetness of the chrome leather shavings. No water is added ...

Embodiment 2

[0041] Preparation of lignin protein filled retanning agent:

[0042] First, add 0-140 parts by mass of water, 250 parts of chrome leather shavings and 65 parts of sodium hydroxide into the reactor, stir for 5 minutes, add the second part of 250 parts of chrome leather shavings and 65 parts of sodium hydroxide , stirred for 5 minutes, then added 250 parts of the 3rd part of chrome leather shavings and 60 parts of sodium hydroxide, stirred for 20 minutes, and the reactant was a uniform paste. Add 75 parts of ammonium lignosulfonate, and continue stirring for 12 hours. Then 60 parts of formic acid are added dropwise in a trickle, and the control time is 3 hours, and then 100 parts of sulfuric acid are added dropwise in a trickle, and the control time is 3 hours. Check the pH value of the 1:10 aqueous solution of the reactants to be 7.5 to 8.0.

[0043] Retanning process:

[0044] Water washing: Put the shaved blue skin and 150% water of the weight of the blue skin into the dr...

Embodiment 3

[0051] Preparation of lignin protein filled retanning agent:

[0052] First, add 0-140 parts by mass of water, 280 parts of chrome leather shavings and 60 parts of sodium hydroxide into the reactor, stir for 5 minutes, add the second part of 280 parts of chrome leather shavings and 55 parts of sodium hydroxide , stirred for 5 minutes, then added 280 parts of the third part of chrome leather shavings and 55 parts of sodium hydroxide, stirred for 20 minutes, and the reactant was a uniform paste. Add 70 parts of ammonium lignosulfonate, and continue stirring for 12 hours. Then add 50 parts of formic acid dropwise in a trickle for a control time of 3 hours, then add 80 parts of sulfuric acid dropwise in a trickle for a control time of 3 hours. Check the pH value of the 1:10 aqueous solution of the reactants to be 7.5 to 8.0.

[0053] Retanning process:

[0054] Water washing: Put the shaved blue skin and 170% water of the weight of the blue skin into the drum, and then add 0.10...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention relates to a novel process for leather tanning. The process course includes watering, neutralizing, dyeing, fatting, fastening, and watering. The main improvement is to use the process castoff chrome leathermeal which is produced during smooth paring as the tanning agent, and other tanning agent as the acrylics and the mimosa extract are compounded simultaneously, and a noveltanning dyeing drum is introduced into, so that the recycle of the waste resource is realized, the environment pollution is reduced, the electric consumption and the energy consumption are saved, andthe cost is lowered.

Description

technical field [0001] The invention belongs to the field of tanning, in particular to a new leather retanning process. Background technique [0002] The existing basic process of tanning is as follows: pre-tanning raw material hides, then chrome tanning, washing with water after wet blue leather, squeezing water, peeling, and then chrome retanning, alkali extraction and neutralization, dyeing and fatliquoring , and finally fix the color and finish the finished leather. There are following technical defects in the above-mentioned prior art: 1. produce a large amount of chromium-containing wastes---chrome leather shavings in the smoothing process, and only my country just produces about 280,000 tons of chromium-containing wastes every year, and the most suitable for chrome leather shavings at present The best treatment method is to landfill it, which not only occupies land resources, but also brings environmental pollution; 2. This process produces a large amount of industria...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C14C3/00
Inventor 宣宏瑜
Owner 鹤山腾泰皮革有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka